© 2019 IBRACON Volume 12, Number 1 (February 2019) p. 31 – 38 • ISSN 1983-4195 http://dx.doi.org/10.1590/S1983-41952019000100005 Efects of Bacillus subtilis biocementation on the mechanical properties of mortars Efeitos da biocimentação promovida por Bacillus subtilis nas propriedades mecânicas de argamassas a State University of Londrina, Department of Building Construction, Londrina, PR, Brazil. Received: 04 Aug 2017 • Accepted: 07 May 2018 • Available Online: This is an open-access article distributed under the terms of the Creative Commons Attribution License N. SCHWANTES-CEZARIO a nicoleschwantes@hotmail.com https://orcid.org/0000-0002-3254-6396 M. F. PORTO a mfeernanda.porto@hotmail.com https://orcid.org/0000-0002-9313-1215 G. F. B. SANDOVAL a gersson.barreto@gmail.com https://orcid.org/0000-0002-8702-8844 G. F. N. NOGUEIRA a geovanasouzanogueira@gmail.com https://orcid.org/0000-0002-7059-257X A. F. COUTO a alissoncouto@ymail.com https://orcid.org/0000-0002-7998-7973 B. M. TORALLES a betoralles@gmail.com http://orcid.org/0000-0001-8828-7250 Abstract Resumo This study aims to evaluate the infuence of B. subtilis AP91 spores addition on the mechanical properties of mortars. B. subtilis strain AP91, isolated from rice leaves of the needle variety, which has an early cycle of production, was used at the concentration of 105 spores/mL in mortars with cement-to-sand ratio of 1:3 (by weight) and water-to-cement ratio (w/c) of 0.63. These spores were added in two diferent ways: in the mixing water and by immersion in a solution containing bacterial spores. Scanning Electron Microscope (SEM) analysis showed crystals with calcium peaks on the EDS, which possibly indicates the presence of bioprecipitated calcium carbonate. The results obtained in the mechanical analysis showed that the bioprecipitation of CaCO 3 by B. subtilis strain AP91 was satisfactory, particularly when the spores were added in the mixing water, increasing the compressive strength up to 31%. Thus, it was concluded that the addition of B. subtilis AP91 spores in the mixing water of cement mortars induced biocementation, which increased the compressive strength. This bioprecipitation of calcium carbonate may very well have other advantageous consequences, such as the closure of pores and cracks in cementitious materials that could improve durability properties, although more research is still needed on this matter. Keywords: calcium carbonate, biocementation, B. subtilis, mechanical properties, SEM. Este estudo tem como objetivo avaliar a infuência da adição de esporos de B. subtilis AP91 nas propriedades mecânicas de argamassas. Para tanto, a bactéria B. subtilis AP91 isolada de folhas de arroz da variedade agulha precoce foi utilizada na concentração de 105 esporos/mL em argamassas com traço de 1:3 (em massa) e relação água/cimento (a/c) de 0,63. Os esporos bacterianos foram adicionados de duas diferentes formas: na água de amassamento e por imersão em solução contendo os esporos. A análise por Microscopia Eletrônica de Varredura (MEV) com Sistema de Energia Dispersiva (EDS) mostrou cristais com picos de cálcio, o que possivelmente indica a presença de carbonato de cálcio bioprecipitado. Os resultados obtidos a partir da análise mecânica mostraram que a bioprecipitação de CaCO 3 pela bactéria B. subtilis AP91 foi satisfatória, particularmente quando os esporos foram adicionados à água de amassamento, aumentando a resistência à compressão em até 31%. Portanto, conclui-se que a adição de esporos de B. subtilis AP91 na água de amassamento das argamassas induziu a biocimenta- ção, que aumentou a resistência à compressão. A bioprecipitação de carbonato de cálcio pode ter outras consequências benéfcas, como o fechamento de poros e fssuras em materiais cimentícios, que poderiam melhorar a durabilidade, embora mais pesquisas neste aspecto ainda sejam necessárias. Palavras-chave: carbonato de cálcio, biocimentação, B. subtilis, propriedades mecânicas, MEV.