JURNAL REKAYASA MESIN VOL. 21 No. 2 September 2021 67 ANALISIS KERUSAKAN PADA BUSHING APRON FEEDER Abraham Partogi Hutabarat (1) , Nurhabibah Paramitha (1*) dan Diah Kusuma Pratiwi (1) (1) Jurusan Teknik Mesin Universitas Sriwijaya (*) E-mail Corresponding Author : nhparamitha@ft.unsri.ac.id Abstrak Industri pertambangan khususnya pada pertambangan batubara memiliki proses pengangkutan dan pengiriman dari suatu lokasi kelokasi lainnya. Pada proses pengangkutan biasanya terdapat kendala yang disebabkan oleh kerusakan pada komponen sehingga dapat menghambat proses pengiriman. salah satu alat pengangkut yang sering mengalami kegagalan adalah Apron Feeder. Proses kerja yang bekerja secara terus menerus dan pembebanan secara berulang-ulang dapat mengalami kerusakan pada komponen-komponen pada Apron Feeder, salah satu komponen yang sering mengalami kerusakan adalah Bushing. Penelitian ini bertujuan untuk menganalisa dan mengetahui penyebab kerusakan yang terjadi pada Bushing Apron Feeder. Metode dari penelitian ini yaitu dengan melihat struktur mikro dari material, nilai kekerasan dari material, melihat cacat permukaan menggunakan dye penetrant. Dengan hasil yang didapat yaitu banyaknya kecacatan berupa goresan dan porositas pada Bushing bagus yang dapat menjadi penyebab kerusakan pada Bushing dan pada Bushing rusak terdapat martesit yang menunjukkan Bushing mengalami deformasi dan getas yang diakibatnya operasional yang dapat menjadi penyebab kerusakan pada Bushing serta pada hasil pengujian XRF (X-Ray Fluorescence) komposisi material pada Bushing terbuat dari AISI 4140 dimana terdaoat perbedaan komposisi pada spesifikasi asli material yaitu SCM 415. Kata Kunci: Pengujian Dye Penetrant, Pengujian XRF, Bushing, Apron Feeder, Analisa Kegagalan, Pengujian Kekerasan , Pengujian Metalografi Abstract The mining industry, especially coal mining, has a transportation and delivery process from one location to another. In the transportation process, there are usually obstacles caused by damage to components that can hinder the delivery process. One of the transportation equipment that often fails is the Apron Feeder. The work process that works continuously and repeated loading can damage the components on the Apron Feeder, one of the components that are often damaged is the Bushing. This study aims to analyze and determine the causes of damage to the Apron Feeder Bushing. The method of this research is by looking at the microstructure of the material, the hardness value of the material, seeing surface defects using a dye penetrant. With the results obtained, namely the number of defects in the form of scratches and porosity in good Bushings which can be the cause of damage to the Bushings and on damaged Bushings, there is martensite which shows that the Bushing is deformed and brittle which results in operations which can be the cause of damage to the Bushing and the results of XRF testing ( X-Ray Fluorescence) the composition of the material on the Bushing is made of AISI 4140 where there is a difference in composition in the original specification of the material, namely SCM 415. Keywords: Dye Penetrant Testing, XRF Testing, Bushing, Apron Feeder, Failure Analysis, Vickers Hardness Testing, Metallography Testing 1. PENDAHULUAN Industri pertambangan khususnya pada pertambang an batubara memiliki proses pengangkutan dan pengiriman dari suatu lokasi kelokasi lainnya. Pada proses pengangkutan biasanya terdapat kendala yang disebabkan oleh kerusakan pada komponen sehingga dapat menghambat proses pengiriman. salah satu alat pengangkut yang sering mengalami kegagalan adalah Apron Feeder. Proses kerja yang bekerja secara terus menerus dan pembebanan secara berulang-ulang dapat mengalami kerusakan pada komponen- komponen pada Apron Feeder, salah satu komponen yang sering mengalami kerusakan adalah Bushing. Penelitian ini bertujuan untuk menganalisa dan mengetahui penyebab kerusakan yang terjadi pada Bushing Apron Feeder.