69 Jurnal Ilmiah Teknosains, Vol. 4 No.2 November 2018 p-ISSN 2460-9986 e-ISSN 2476-9436 KAJIAN KUAT TEKAN PAPERCRETE MUTU TINGGI DENGAN BAHAN TAMBAH LIMBAH KERAMIK Hendramawat Aski Safarizki 1) , Iwan Ristanto 2) 1) Fakultas Teknik, Program Studi Teknik Sipil, Universitas Veteran Bangun Nusantara, Sukoharjo, Jl. Letjen Sudjono Humardhani, No.1, Jombor, Sukoharjo; Telp. 0271-593156. Email: hendra.mawat@gmail.com 2) Fakultas Teknik, Program Studi Teknik Sipil, Universitas Veteran Bangun Nusantara, Sukoharjo, Jl. Letjen Sudjono Humardhani, No.1, Jombor, Sukoharjo; Telp. 0271-593156. Email: iwan.ristanto@yahoo.com Abstrak Papercrete merupakan alternatif beton ringan dengan memanfaatkan limbah kertas yang ada di sekitar kita. Kelemahan dari papercrete adalah mutu kuat tekan yang rendah dikarenakan bahan penyusunnya yang berupa kertas. Target dari penelitian ini adalah merumuskan rancang campur (mix design) dari papercrete mutu tinggi yang tahan terhadap beban dengan bahan tambah limbah keramik yang ramah lingkungan. Dengan memanfaatkan limbah keramik maka dapat mengurangi pencemaran pada lingkungan sekaligus meningkatkan kuat tekan papercrete. Metode yang dipakai dalam penelitian ini adalah uji rancang campur pada laboratorium sehingga didapatkan komposisi campuran mutu tinggi antara papercrete dengan limbah keramik. Tahapan penelitian dimulai dengan pembuatan papercrete dengan tanpa bahan tambah limbah keramik. Kadar campuran kertas yang digunakan adalah 0%, 20%, 20% dan 30% dari volume pasir yang digunakan. Pada penelitian dibuat juga papercrete dengan bahan tambah limbah keramik. Kadar keramik pada campuran papercrete yang digunakan adalah 0%, 20%, 20% dan 30% dari jumlah pasir yang digunakan. Kesimpulan yang dapat diperoleh dari hasil pengujian adalah bahan tambah limbah keramik dapat meningkatkan kuat tekan papercrete. Nilai kuat tekan optimum pa- percrete tanpa bahan tambah limbah keramik dan papercrete dengan bahan tambah limbah keramik berada pada angka 26,0 MPa - 26,3 MPa. Kata kunci: beton ringan, keramik, mix design, papercrete Abstract Papercrete was a lightweight concrete alternative by utilizing paper waste around us. The disadvantage of papercrete is the low quality of compres- sive strength because the constituent material is paper. The aim of this study is to formulate a mix design of high quality papercrete with ceramic waste that environmentally friendly. By utilizing ceramic waste, it can reduce pollution in the environment while increasing the compressive strength of papercrete. The method used in this study is a mixed design test in the laboratory so that a high quality mixture composition between papercrete and ceramic waste is obtained. The research phase begins with making papercrete without ceramic waste. The paper content used is 0%, 20%, 20% and 30% of the volume of sand in the concrete mixture. In this study papercrete was also made by adding ceramic waste material. Ceramic content in the papercrete mixture is 0%, 20%, 20% and 30% of the amount of sand used in the mixture. The conclusion that can be obtained from the test results is ceramic waste can increase the compressive strength of papercrete. The optimum compressive strength of papercrete without the added material of ceramic waste and papercrete with the added material of ceramic waste at a value of 26.0 MPa - 26.3 MPa. Keywords: ceramic, lightweight concrete, mix design, papercrete 1. PENDAHULUAN Perkembangan teknologi beton saat ini sudah sangat pesat. Pemilihan beton ringan mutu tinggi sebagai pengganti beton konvensional sudah mulai dikembangkan peneliti. Papercrete merupakan salah satu dari alternatif beton ringan yang dapat digunakan sebagai elemen struktur pada bangunan. Papercrete merupakan hasil penggabungan antara beton dengan kertas sehingga didapatkan material beton yang kuat namun ringan dari segi berat sendiri komponen penyusunnya. Komponen penyusun papercrete adalah semen, pasir dan kertas. Penelitian tentang papercrete mulai banyak dilakukan oleh para ahli di bidang rekayasa beton. Sampah kertas di Indonesia dengan asumsi laju produksi sampah 2 liter/orang/hari dan komposisi 6,17% maka jumlah timbulan sampah kertas dapat mencapai 1.599.00 ton/tahun. Hanya sekitar 10 % dari sampah tersebut yang didaur ulang kembali. Pemanfaatan limbah kertas yang jumlah dan potensinya cukup besar belum optimal dilakukan (Wahyono, 2001). Kertas bekas dapat dimanfaatkan sebagai bahan dari papercrete sehingga ikut mengurangi sampah kertas di muka bumi. Papercrete dapat dengan mudah dibentuk salah satunya adalah digunakan sebagai bata. Bata dari papercrete ringan dan mudah dalam finishing arsitektur. Bata dari bahan papercrete dapat digunakan sebagai struktur dinding non struktural (Myriam, 2017). Dengan bentuknya yang mudah disesuaikan maka papercrete dapat mengikuti kebutuhan dari stuktur yang diinginkan. Bata papercrete adalah material kedap suara yang baik sehingga dapat digunakan sebagai elemen gedung