Harmiansyah, dkk./ Jurnal Teknik Mesin Indonesia, Vol. 17 No. 2 (Oktober 2022) Hal. 87-92 87 | JTMI Studi awal material komposit berpenguat serat bambu dengan matriks resin epoksi/hardener sebagai material antipeluru Harmiansyah 1 , Burmawi 2 , Risky Arman 2 , Rustam Efendi 3 1 Program Studi Teknik Biosistem, Jurusan Teknologi Produksi dan Industri, Institut Teknologi Sumatera Jl. Terusan Ryacudu, Lampung Selatan, Lampung, Indonesia, 35365 2 Jurusan Teknik Mesin, Fakultas Teknologi Industri, Universitas Bung Hatta Jl. Gajah Mada No. 19 Olo Nanggalo Padang, Sumatera Barat 25143 3 Jurusan Teknik Mesin, Fakultas Teknik, Universitas Sulawesi Tenggara Jl. Kapten Piere Tendean No. 109 A, Baruga, Kendari, Sulawesi Tenggara, Indonesia, 93563 Email korespondensi: harmibm@gmail.com Abstrak Material antipeluru digunakan sebagai material rompi antipeluru yang berfungsi melindungi tubuh manusia dari ancaman serangan fisik, terutama serangan yang berasal dari senjata api. Material antipeluru berfungsi mereduksi energi kinetik dari proyektil, sehingga tidak mengenai pengguna rompi antipeluru. Material utama dalam pembuatan material antipeluru adalah baja dengan massa jenis yang tinggi, sehingga bobot dari material antipeluru tinggi yang menyebabkan pengguna tidak dapat bergerak dengan leluasa. Komposit merupakan material yang terdiri dari dua unsur atau lebih yang memiliki sifat mekanik yang baik serta densitas yang rendah, sehingga dapat dijadikan alternatif pengganti baja untuk material antipeluru. Material antipeluru yang digunakan berpenguat serat bambu betung dengan matriks campuran resin epoksi/hardener dan penambahan butiran keramik 20, 25 dan 30 ml, material komposit dilakukan pengujian balistik yang menggunakan variasi parameter jarak tembak 2; 2,5; dan 3 m. Berdasarkan hasil uji balistik, semua variasi penambahan butiran keramik mampu mereduksi energi proyektil dengan kedalaman penetrasi < 1 mm, di mana energi kinetik dari proyektil sebesar 209,83 joule. Berdasarkan analisis foto makro jejak proyektil pada material antipeluru, retakan yang terjadi pada material antipeluru adalah retakan ulet karena terjadi penyebaran retakan ke area lain pada permukaan material antipeluru. Kata kunci: serat bambu, material antipeluru, butiran keramik, komposit, resin epoksi/hardener. Abstract Bulletproof material is used as a bulletproof vest material that functions to protect the human body from the threat of physical attack, especially attacks from firearms. Bulletproof material serves to reduce the kinetic energy of the projectile so it does not hit the bulletproof vest user. The main material in the manufacture of bulletproof material is steel with a high density so that the weight of the bulletproof material is high which causes the user to be unable to move freely. Composite is a material consisting of two or more elements that have good mechanical properties and low density so that it can be used as an alternative to steel for bulletproof materials. The bulletproof material used was reinforced with bamboo fiber with a matrix of epoxy resin/hardener mixture and the addition of 20, 25, and 30 ml ceramic granules, the composite material was tested for ballistics using a variation of the firing range parameter 2; 2.5; and 3 m. Based on the results of ballistic tests, all variations of the addition of ceramic granules were able to reduce the energy of the projectile with a penetration depth of < 1 mm where the kinetic energy of the projectile was 209.83 joule. Based on the macro photo analysis of projectile traces on the bulletproof material, the cracks that occur in the bulletproof material are ductile cracks due to the spread of the cracks to other areas on the surface of the bulletproof material. Keywords: bamboo fiber, bullet-proof material, ceramic granules, composite, epoxy/hardener resin. 1. Pendahuluan Komposit merupakan campuran dari dua unsur material atau lebih dengan sifat mekanik yang berbeda, kombinasi dari pencampuran material bertujuan untuk mendapatkan material baru yang memiliki sifat makro-mekanis yang lebih baik. Sifat mekanik yang ditingkatkan dalam pembuatan material komposit antara lain kekuatan, kekakuan, ketahanan aus, ketahanan korosi, fatigue life, ketahanan thermal dan densitas rendah [1]. Penggunaan komposit untuk mendapatkan sifat mekanik yang lebih baik dibandingkan material penyusunnya [2], perkembangan komposit saat ini begitu cepat dan semakin berpotensi menjadi material alternatif pengganti logam. Bahan komposit memiliki keunggulan kuat, ringan, tahan korosi yang baik, dengan karakteristik dan kekuatan mekanis yang sangat tinggi [3]. Komposit yang terdiri dari unsur penguat serat alami bambu memiliki sifat kuat tarik yang baik yaitu