365 KIMIA.STUDENTJOURNAL, Vol. 2, No. 1, pp. 365-371 - UNIVERSITAS BRAWIJAYA MALANG Received, 5 September 2013, Accepted, 10 September 2013, Published online, 5 oktober 2013 OPTIMASI EKSTRAKSI SILIKA DAN ALUMINA DARI LUMPUR SIDOARJO Ahmad Naufal Hasti Eka Putra, Rachmat Triandi Tjahjanto*, Mohammad Misbah Khunur. Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Brawijaya Jl. Veteran Malang 65145 *Alamat korespondensi, Tel : +62-341-575838, Fax : +62-341-575835 Email: rachmat_t@ub.ac.id ABSTRAK Penelitian tentang optimasi ekstraksi silika dan alumina dari lumpur Sidoarjo telah dilakukan. Tujuan dari penelitian ini adalah untuk mengetahui kondisi optimal ekstraksi silika dan alumina dari lumpur Sidoarjo. Untuk mengetahui kondisi optimal ekstraksi, dilakukan variasi konsentrasi dan jenis pelarut. Pelarut HCl dan NaOH digunakan untuk mengekstrak silika dan alumina dari lumpur Sidoarjo. Asam klorida ditambahkan pada filtrat hasil ekstraksi dengan NaOH untuk mengendapkan Al(OH) 3 pada pH 8, kemudian filtrat dikondisikan pada pH 4 dengan HCl untuk mengendapkan Si(OH) 4 . Filtrat hasil ekstraksi mengggunakan HCl ditambah NaOH untuk mengendapkan Fe(OH) 3 pada pH 4, filtrat kemudian ditambahkan NaOH hingga pH 8 untuk mengendapkan Al(OH) 3 . Hasil penelitian menunjukkan bahwa hasil ekstraksi dipengaruhi oleh konsentrasi dan jenis pelarut. Pada penelitian ini, konsnetrasi 6 M merupakan kondisi optimal ekstraksi baik menggunakan asam maupun basa. Kemurnian tertinggi endapan silika diperoleh dari ekstraksi menggunakan NaOH yaitu sebesar 95,6 %. Kata kunci: alumina, ekstraksi, lumpur Sidoarjo, silika. ABSTRACT Optimization of silica and alumina extraction from Sidoarjo mud have studied. The aim of this research is to know the optimum condition of silica and alumina extraction from Sidoarjo mud. Optimum condition of extraction is studied by variying the concentration and solvent used in the extraction process. Hydrochloric acid and NaOH were used in silica and alumina extraction from Sidoarjo mud. Hydrochloric acid was added to the filtrate of NaOH extract to obtain Al(OH) 3 at pH 8, further the HCl added until pH 4 to obtain Si(OH) 4 . The filtrate of HCl extract wad added by NaOH until pH 4 to precipitate Fe(OH) 3 , further NaOH was added until pH 8 to obtain Al(OH) 3 . The result of this experiment shows that extractions result was affected by the concentration and the solvent used. The optimal concentration of solvent for extraction prosses is 6 M for both acid and base. The purest silica in this research was obtained from NaOH extract with the purity level of 95,6%. Key words: alumina, extraction, Sidoarjo mud, silica. PENDAHULUAN Tanggal 27 Mei 2006 telah terjadi semburan lumpur Sidoarjo yang berdampak besar pada kehidupan penduduk dan perekonomian di Jawa Timur [1], kerugian ekonomi yang diakibatkan semburan mencapai Rp 20 miliar perhari sebagai direct cost [2]. Telah dilakukan penelitian tentang lumpur Sidoarjo, kandungan senyawa yang terdapat dalam lumpur Sidoarjo adalah Al 2 O 3 16%, SiO 2 49,9%, K 2 O 2,51%, CaO 6,14%, TiO 2 1,74%, dan Fe 2 O 3 21,7% [3]. Kadar silika dan alumina yang cukup besar dalam lumpur Sidoarjo memungkinkan untuk brought to you by CORE View metadata, citation and similar papers at core.ac.uk provided by Jurnal Ilmu Kimia Universitas Brawijaya