1 Supporting Information: Noncapacitive Hysteresis in Perovskite Solar Cells at Room Temperature Osbel Almora, Clara Aranda, Isaac Zarazua, Antonio Guerrero, and Germà Garcia- Belmonte* Institute of Advanced Materials (INAM), Universitat Jaume I, 12071 Castelló, Spain *Corresponding author: G. Garcia-Belmonte, (garciag@uji.es) tel.: +34 964 387538 3 June 2016 Figure S1: Current density-voltage (J-V) curves for all studied devices measured under one sun (100 mW cm -2 ) AM1.5G illumination in both, forward (FS) and backward (BS), bias scan senses. While RegularFlat and RegularMeso cells exhibit significant hysteresis, the Inverted device has almost no presence of such effect. The scan rate was of 40 mV s -1 .