Dalton : J. Pend. Kim. dan Ilmu. Kim. (e-ISSN 2621-3060) Vol. 7, No. 1, 2024 DOI: http://dx.doi.org/10.31602/dl.v7i1.14360 Uniska PPJ-Daltonjurnal SINTESIS MEMBRAN KITOSAN/POLI VINIL ALKOHOL (PVA) UNTUK MENURUNKAN KADAR LIMBAH PEWARNA TEKSTIL Septiana Ambarwati* 1 ∙ Nur Arifah Hidayati 1 ∙ Henny Parida Hutapea 1 Received: 21 Maret 2024 | Accepted: 28 Maret 2024 | Published online: 30 April 2024 UPT Publikasi dan Pengelolaan Jurnal Uniska-Daltonjurnal 2024 Abstrak Teknologi membran termasuk kedalam clean technology yang sedang dikembangkan saat ini. Membran kitosan dapat diaplikasikan untuk pengolahan limbah industri tekstil. Kombinasi kitosan dengan PVA bertujuan untuk meningkatkan sifat mekanik membran yang dapat dikaji berdasarkan sifat daya serap air dan daya hantar ion membran. Ikatan polimer membran kitosan/PVA tidak terbentuk dengan baik sehingga membuat PVA larut dalam NaOH pada proses pelepasan membran dari cetakan kaca. Sintesis membran dilakukan dengan melarutkan kitosan/PVA dengan variasi komposisi kitosan/PVA (m/m) diantaranya 1:3; 1:1; 3:1. Hasil penelitian menunjukkan analisis water uptake, swelling degree, dan IEC memiliki kecenderungan semakin tinggi dengan adanya peningkatan kadar kitosan dan penurunan kadar PVA. Analisis water uptake dan swelling degree tertinggi dicapai pada komposisi kitosan/PVA 3:1 dengan nilai 9,5% dan 0,36%. Analisis IEC tertinggi dicapai pada nilai 1,25 meq pada komposisi kitosan/PVA 3:1. Kata kunci Kitosan ∙ PVA ∙ water uptake ∙ swelling degree ∙ IEC. This is an open-access article under the CC-BY 4.0 License. Copyright © 2024 by authors.  Septiana Ambarwati email: Saseptiana189@gmail.com 1 Program Studi Kimia Industri, Politeknik Santo Paulus Surakarta Abstract Membrane technology is included in the clean technology that is currently being developed. Chitosan membranes can be applied for processing textile industry waste. The combination of chitosan with PVA aims to improve the mechanical properties of the membrane which can be studied based on the properties of the membrane's water absorption and ion conductivity. The polymer bonds of the chitosan/PVA membrane were not formed properly, causing the PVA to dissolve in NaOH during the process of removing the membrane from the glass mold. Membrane synthesis was carried out by dissolving chitosan/PVA with variations in the composition of chitosan/PVA (m/m) including 1:3; 1:1; and 3:1. The research results showed that water uptake, swelling degree, and IEC analysis had a tendency to be higher with increasing chitosan levels and decreasing PVA levels. The highest water uptake and swelling degree analysis was achieved with a 3:1 chitosan/PVA composition with values of 9.5% and 0.36%. The highest IEC analysis was achieved at a value of 1.25 meq at a 3:1 chitosan/PVA composition. Keywords Chitosan ∙ PVA ∙ Water Uptake ∙ Swelling Degree ∙ IEC. PENDAHULUAN Pencemaran lingkungan menjadi perhatian dari berbagai kalangan, terutama pencemaran limbah industri tekstil. Zat pencemar menyebabkan pencemaran air sehingga menurunkan kualitas air. Zat pencemar banyak ditemukan di industri tekstil karena industri tekstil lebih memilih menggunakan pewarna sintetis karena warna yang variatif dan penggunaan yang praktis. Proses pewarnaan berpotensi menghasilkan limbah yang dibuang ke lingkungan sekitar 10- ORIGINAL ARTICLE