N Soltani et al.: he simultaneous efect of extrusion and T6 treatment HTM J. Heat Treatm. Mat. 67 (2012) 6 (formerly HTM Z. Werkst. Wärmebeh. Fertigung) 1 1 Introduction he growing demand to reduce energy consumption by develo- ping more fuel eicient vehicles is a challenge for the automoti- ve industry. Recently, a large number of metal matrix composites (MMCs) have been developed for high-performance applications in automotive industries. he properties of particulate metal ma- trix composites (PMMCs) make them ideal candidates to replace steel and iron in the automotive industry. Al-based composites reinforced with particulates of Mg 2 Si have been introduced as a new group of composites that ofer attractive advantages such as low density, good wear resistance and good castability [1]. hey N. Soltani, A. Bahrami, F. M. Moghimi, A. Hajaghasi he simultaneous efect of extrusion and T6 treatment on the mechanical properties of Al-15wt.%Mg 2 Si compositet Der Efekt von Strangpressen und T6-Behandlung auf die mechanischen Eigenschaten eines Al-15 Ma.-%Mg 2 Si-Verbundwerkstofs Abstract/Kurzfassung his article investigates the simultaneous efect of extrusion ratio and T6 heat treatment on microstructure and mecha- nical properties of in-situ Al-15wt.%Mg 2 Sii composite. his composite has already been introduced as a new class of light materials but the brittle structure of the primary Mg 2 Si which is formed during solidiication limits its application. As-cast composite was directly extruded as rod by using three dife- rent dies. Ater T6 heat treatment on extruded samples, mi- crostructure was studied by optical and scanning electron mi- croscopy. Results demonstrated that extruded and heat treated composite possesses considerably higher strength and enhan- ced ductility in comparison with the as-cast samples. It was also found that heat treatment and extrusion processes change the primary Mg 2 Si morphology considerably and its size in- creases as extrusion ratio decreased. Fracture surface exami- nations revealed a transition from brittle fracture mode in as- cast composite to ductile fracture in heat treated and extruded specimens. his can be attributed to the changes in size and morphology of Mg 2 Si intermetallics and porosity content. n Keywords: Aluminum matrix composite, hot extrusion, T6 heat treatment, mechanical properties Authors/Autoren: N. Soltani, MSc. Graduate Student, Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran A. Bahrami, MSc. Graduate Student, Razi Metallurgical Research Center, Tehran, Iran, amin.bah@gmail.com (Corresponding author/Kontakt) F. M. Moghimi, A. Hajaghasi, MSc. Graduate Student, Department of Engineering, Saveh Branch, Islamic Azad University, Saveh, Iran Die vorliegende Arbeit untersucht den kombinierten Ein- luss verschiedener Umformgrade beim Strangpressen und einer T6-Wärmebehandlung auf Gefüge und mechanische Eigenschaten eines Al-15 Ma.-%Mg2Si-Verbundwerkstofs. Dieser gehört zu einer bereits bekannten Klasse neuer Leicht- bauwerkstofe, deren Einsatzbereich jedoch durch die Sprö- digkeit der primären Mg2Si-Partikel, die sich während der Erstarrung bilden, eingeschränkt ist. Das gegossene Ausgangs- material wurde mithilfe von drei verschiedenen Stempeln di- rekt in Stangenform gepresst. Nach der T6-Wärmebehandlung an extrudierten Proben wurde die Mikrostruktur durch Licht- und Rasterelektronenmikroskopie untersucht. Die Ergebnisse zeigten, dass extrudierte und wärmebehandelte Proben we- sentlich höhere Festigkeit und erhöhte Duktilität im Vergleich zu den Proben im gegossenen Zustand besitzen. Ferner wurde beobachtet, dass Prozesse, die Strangpressen und Wärmebe- handlung kombinieren, die Morphologie der primären Mg2Si- Ausscheidungen signiikant verändern, wobei ihre Größe mit abnehmendem Umformgrad ansteigt. Eine Untersuchung der Bruchlächen zeigte einen Übergang des Bruchmodus von Sprödbruch beim Ausgangsmaterial zu duktilem Bruch in den extrudierten und wärmebehandelten Proben. Dies kann den Änderungen der Größe und Morphologie der Mg2Si Phasen und der Porosität zugeschrieben werden. n Schlüsselwörter: Aluminiummatrix-Verbundwerkstof, Warmstrangpressen, T6-Wärmebehandlung, mechanische Eigenschaten HT110158