Conductivite eÂlectrique membranaire: eÂtude de l'eet de la concentration, de la nature de l'eÂlectrolyte et de la structure membranaire R. Lteif, L. Dammak, C. Larchet *, B. Auclair Laboratoire des Mate Âriaux Echangeurs d'ions, Universite  Paris-Val de Marne, 94010 Cre Âteil, France Received 27 July 1998; accepted 11 August 1998 Re sume Nous avons eÂtudie les variations de la conductivite eÂlectrique membranaire mesureÂe en courant alternatif en fonction de la concentration d'eÂquilibrage C e , de la nature du contre-ion et de la nature de la membrane. Sept membranes eÂchangeuses de cations, reÂparties en trois cateÂgories, sont utiliseÂes: CM1, CM2 et CMx; Na®on 1 117 et Na®on 1 324; MK-40 et CRP. Les mesures sont reÂaliseÂes dans trois milieux dieÂrents (NaCl, KCl et LiCl), leur concentration allant geÂneÂralement de 0,01 aÁ 2 M. Les reÂsultats expeÂrimentaux montrent que les membranes MK-40, CRP, Na®on 1 117 et Na®on 1 324 preÂsentent des comportements particuliers speÂci®ques de leurs cateÂgories. Dans le domaine des fortes concentrations, les conductiviteÂs des membranes MK-40 et CRP continuent d'augmenter de fac ° on sensible avec la concentration. Ce pheÂnomeÁne peut s'interpreÂter par les caracteÂristiques structurelles de ces membranes: une faible capacite d'eÂchange et un gon¯ement important speÂci®que des membranes heÂteÂrogeÁnes. De leur coà teÂ, les membranes Na®on 1 117 et Na®on 1 324 pre sentent la particularite de donner des rapports de conductivite k (K + )/k (Li + ) infeÂrieurs aÁ ceux des conductiviteÂs ioniques eÂquivalentes des contre-ions en solution. Nous avons montre que ce comportement peut eÃtre explique par leur structure interne deÂcrite par le modeÁle de Gierke. # 1999 Elsevier Science Ltd. All rights reserved. Abstract We have studied the variation of the membrane electric conductivity measured under alternative current, as a function of the equilibrating concentration, C e , of the counter-ion nature and of the membrane type. Seven cation exchange membranes, distributed into three categories, were used: CM1, CM2 and CMx; na®on 1 117 and Na®on 1 324; MK-40 and CRP. The measurements were achieved with three dierent electrolytes (NaCl, KCl and LiCl), the concentration varying generally from 0,01 to 2 M. The experimental results show that the MK-40, CRP, Na®on 1 117 and Na®on 1 324 membranes present a particular behaviour speci®c to their categories. In high ranges of concentration, the conductivities of MK-40 and CRP membranes continue to increase in a sensitive way with concentration. This phenomenon can be interpreted by the structural characteristics of the membranes. On the other side, the Na®on 1 117 and Na®on 1 324 membranes present the particularity of their given conductivity ratios k(K + )/k(Li + ) which are lower than their equivalent ionic conductivitie ratios in solution. We have shown that this behaviour can be explained by their internal structure as described by the Gierke model. # 1999 Elsevier Science Ltd. All rights reserved. European Polymer Journal 35 (1999) 1187±1195 0014-3057/99/$ - see front matter # 1999 Elsevier Science Ltd. All rights reserved. PII: S0014-3057(98)00213-4 PERGAMON * Corresponding author. E-mail: larchet@univ-paris12.fr