KOVALEN: Jurnal Riset Kimia, 6(2), 2020: 90-98 90 Paramitha & Sitompul Karakterisasi Nanokomposit Poly(Lactic Acid)-Spent Bleaching Earth Regenerasi Termodifikasi [Characterization of Nanocomposite of Poly(Lactic Acid)-Modified Regenerated Spent Bleaching Earth] Tika Paramitha 1* dan Johnner P. Sitompul 2 1) Program Studi Teknik Kimia, Fakultas Teknik, Universitas Sebelas Maret, 57126, Surakarta, Jawa Tengah, Indonesia 2) Program Studi Teknik Kimia, Fakultas Teknologi Industri, Institut Teknologi Bandung, Jawa Barat, Indonesia * ) Corresponding Author: tikaparamitha@staff.uns.ac.id (hp/fax: +6287758189404) ABSTRACT. Development of renewable resource-based polymers attracts attention to solve environmental problems due to the build up of polymer (plastic). Poly(lactic acid) (PLA) is one of the most widely used polymers which have good biodegradability and processability. The addition of fillers to the PLA matrix aims to improve the characteristics of the PLA, such as mechanical properties of nanocomposites of PLA. Thus, PLA can be use as substitution of fossil fuel-based polymer. Spent Bleaching Earth (SBE) can be used as a filler after regeneration process. SBE was extracted and oxidized to take its oil content. Then, SBE was modified with urea solution to increase the interlayer distance. In this study, structure of nanocomposites was characterized using X-Ray Diffraction and mechanical properties of nanocomposites were characterized using Universal Testing Machines. X-Ray Diffraction characterization results show that PLA-SBE nanocomposite and PLA-modified regenerated SBE nanocomposites do not form new peaks, so SBE and modified regenerated SBE is intercalated and partially exfoliated in the PLA matrix. The degree of intercalation/exfoliation is indicated by the results of characterization of mechanical properties. The mechanical properties of PLA-SBE nanocomposite are lower than neat PLA, whereas the mechanical properties of PLA-modified regenerated SBE nanocomposites are higher than neat PLA. The best mechanical properties of nanocomposites were obtained for PLA-5% modified regenerated SBE, with elongation and tensile strength, 3.26% and 42.22 MPa, respectively. Keywords: nanocomposites, poly(lactic acid), regeneration, spent bleaching earth ABSTRAK. Pengembangan polimer berbasis sumber daya terbaharukan menarik perhatian untuk menyelesaikan permasalahan lingkungan akibat penumpukan polimer (plastik). Poly(lactic acid) (PLA) adalah salah satu polimer yang banyak digunakan yang memiliki keunggulan mudah terdegradasi dan mudah dalam pemrosesan. Penambahan bahan pengisi pada matrik PLA bertujuan untuk meningkatkan karakteristik PLA, seperti sifat mekanis nanokomposit PLA. Sehingga, PLA dapat digunakan sebagai substitusi polimer berbasis sumber daya bahan bakar fosil. Spent Bleaching Earth (SBE) dapat digunakan sebagai bahan pengisi setelah dilakukan proses regenerasi. SBE diekstraksi dan dioksidasi untuk mengambil kandungan minyaknya. Selanjutnya, SBE dimodifikasi dengan larutan urea untuk meningkatkan jarak interlayernya. Pada penelitian ini, struktur nanokomposit dikarakterisasi menggunakan X-Ray Diffraction dan sifat mekanik nanokomposit dikarakterisasi menggunakan Universal Testing Machine. Hasil karakterisasi X-Ray Diffraction menunjukkan bahwa nanokomposit PLA-SBE dan PLA-SBE regenerasi termodifikasi tidak terbentuk puncak baru, sehingga SBE dan SBE regenerasi termodifikasi terinterkalasi dan sebagian tereksfoliasi pada matrik PLA. Derajat interkalasi/eksfoliasi tersebut ditunjukkan dengan hasil karakterisasi sifat mekanik. Sifat mekanik nanokomposit