REVISTA DE METALURGIA April–June 2020, 56 (2), e170 ISSN-L: 0034-8570 https://doi.org/10.3989/revmetalm.170 Flow stress behaviour and microstructural analysis of hot deformed Aluminium matrix composites reinforced with CuZnAlNi shape memory alloy particles Kenneth K. Alaneme a,b,* , Michael O. Bodunrin a,b,c , Lesley H. Chown c,d , Nthabiseng B. Maledi c a Materials Design and Structural Integrity Research Group, Department of Metallurgical and Materials Engineering, Federal University of Technology, Akure, P.M.B. 704, Ondo State, Nigeria b Department of Metallurgical and Materials Engineering, Federal University of Technology, Akure, P.M.B. 704, Ondo State, Nigeria c School of Chemical and Metallurgical Engineering, University of the Witwatersrand, Private Bag 3, WITS, 2050, Johannesburg, South Africa d DST-NRF Centre of Excellence in Strong Materials, University of the Witwatersrand, Private Bag 3, WITS, 2050, Johannesburg, South Africa * Corresponding author: kalanemek@yahoo.co.uk Submitted: 27 September 2019; Accepted: 10 February 2020; Available On-line: 28August 2020 ABSTRACT: The compressive flow stress behaviour and microstructures of hot deformed Al alloy matrix com- posites (AMCs) reinforced with CuZnAlNi based shape memory alloy (SMA) particles was investigated. Al-Mg-Si based alloy, reinforced with 4, 6, and 8 wt.% Cu-18Zn-7Al-0.3Ni, and 8 wt.% SiC particles, were produced by double stir casting and subjected to hot compression testing at 1.0 s -1 strain rate, 400 °C temperature, and ~ 60% constant global strain using a Gleeble 3500 thermomechanical simulator. The starting and as-deformed micro- structures of the composites were examined using optical microscopy. The use of Cu-18Zn-7Al-0.3Ni particles as reinforcement resulted in the development of finer matrix structure compared with the use of SiC. The flow stress and hardness of the AMCs reinforced with Cu-18Zn-7Al-0.3Ni particles were generally higher than that of the unreinforced Al alloy and the SiC reinforced Al alloy. Also the flow stress, and to a large extent the hardness, increased with increase in the weight percent of Cu-18Zn-7Al-0.3Ni particles in the AMC. The improvement observed with the use of Cu-18Zn-7Al-0.3Ni alloy particles was ascribed to the combination of enhanced matrix grain refinement strengthening, interfacial strengthening, compressive residual stresses, high thermal conductiv- ity, and damping capacity offered by the Cu-18Zn-7Al-0.3Ni alloy. KEYWORDS: CuZnAlNi alloy; Flow stress; Hot deformation; Microstructure; Shape memory alloy reinforced Al based composites; Strengthening mechanism Citation/Citar como: Alaneme, K.K.; Bodunrin, M.O.; Chown, L.H.; Maledi, N.B. (2020). “Flow stress behaviour and microstructural analysis of hot deformed Aluminium matrix composites reinforced with CuZnAlNi shape memory alloy particles”. Rev. Metal. 56(2): e170. https://doi.org/10.3989/revmetalm.170 RESUMEN: Comportamiento del flujo de esfuerzo y análisis microestructural de compuestos de matriz de aluminio deformados en caliente y reforzados con partículas de la aleación con memoria de forma CuZnAlNi. Se investigó el comportamiento del flujo de esfuerzo por compresión y las microestructuras de los compuestos de matriz de aleación de Al deformada en caliente (AMC) y reforzados con partículas de la aleación con memoria de forma (SMA) basadas en CuZnAlNi. La aleación base Al-Mg-Si reforzada con 4, 6 y 8% en peso de Cu-18Zn-7Al- 0,3Ni, y 8% en peso de partículas de SiC, se obtuvieron mediante agitación doble y se sometieron a pruebas de compresión en caliente a una velocidad de deformación de 1,0 s −1 , temperatura de 400 °C, y ~60% de defor- mación global constante, para ello se utilizó un simulador termo-mecánico Gleeble 3500. Las microestructuras iniciales y deformadas de los compuestos se examinaron utilizando microscopía óptica. El uso de partículas Cu-18Zn-7Al-0,3Ni como refuerzo dio como resultado el desarrollo de una estructura de matriz más fina en comparación con el SiC. La tensión de flujo y la dureza de los AMC reforzados con partículas de Cu-18Zn-7Al- 0,3Ni fueron generalmente más altos que los de la aleación de Al no reforzada y la aleación de Al reforzada con SiC. También la tensión de flujo y, en gran medida, la dureza creció con el aumento en el porcentaje en peso de partículas de Cu-18Zn-7Al-0,3Ni en el AMC. La mejora observada con el uso de partículas de la aleación