Sifat Optik Campuran Pasta TiO 2 Partikel Nano dan Pasta TiO 2 Reflektor pada Foto Elektroda Dye Solar Cell Optical Properties of Blending Paste of TiO 2 Nanoparticles and TiO 2 Reflector for Dye Solar Cell’s Photoelectrode Lilis Retnaningsih*, Lia Muliani, dan Goib Wiranto Pusat Penelitian Elektronika dan Telekomunikasi, Lembaga Ilmu Pengetahuan Indonesia Komplek LIPI Gedung 20 Lantai 4, Jl Sangkuriang, Bandung 40135, Indonesia Abstrak Dalam penelitian ini, kami mengamati pengaruh dari campuran pasta TiO 2 partikel nano dan pasta TiO 2 reflektor yang dapat meningkatkan kinerja dye-sensitized solar cell (DSSC). Senyawa TiO 2 reflektor ini berfungsi sebagai lapisan penghambur, yang diharapkan dapat meningkatkan kinerja DSSC. Dalam penelitian ini, foto elektroda DSSC dibuat dengan mencampurkan bahan pasta TiO 2 partikel nano dan bahan pasta TiO 2 reflektor dengan rasio dari dua bahan tersebut yang telah ditentukan. Pasta pertama adalah campuran dari bahan utama dan bahan pencampur dengan perbandingan antara pasta TiO 2 partikel nano dan pasta TiO 2 reflektor sebesar 95% : 5%, pasta kedua adalah campuran dengan perbandingan 90% : 10%, dan pasta ketiga dengan perbandingan 85% : 15%. Pasta hasil campuran kemudian dilapiskan pada permukaan kaca konduktif yang memiliki dimensi konduktif sebesar 1 cm x 1 cm. Sel surya DSSC hasil proses pabrikasi kemudian diukur menggunakan I-V measurement system dan Sun simulator untuk mengetahui arus, tegangan, dan efisiensi yang dihasilkan. Lapisan foto elektroda DSSC diukur dengan menggunakan UV - Visible absorbance untuk menentukan karakteristik daya serapnya terhadap cahaya yang datang pada permukaan TiO 2 hasil pencampuran. Kami juga telah melakukan pengukuran menggunakan alat SEM (scanning electron microscope) untuk mengetahui karakteristik permukaan hasil pencampuran kedua jenis pasta yang telah digunakan. Hasil pengukuran menunjukkan bahwa DSSC hasil pencampuran pasta dengan perbandingan 85% pasta TiO 2 partikel nano terhadap 15% pasta TiO 2 reflektor memiliki ukuran partikel yang paling besar dan menghasilkan efisiensi yang paling besar pula. Kata kunci: dye-sensitized solar cell, pasta TiO 2 reflektor, lapisan penghambur, pasta TiO 2 partikel nano. Abstract In this research, we investigate the effect of the blends of TiO 2 nanoparticle paste and TiO 2 reflector paste which can improve the performance of dye-sensitized solar cell (DSSC). Reflector TiO 2 compound serves as a scattering layer which is expected to be able to improve the performance of DSSC. In this research, the dye solar cell’s photoelectrode was fabricated by mixing TiO 2 reflector paste into TiO 2 nanoparticles paste with a ratio of these two ingredients which have been determined. The first blending paste ingredients with a comparison between TiO 2 nanoparticles paste and TiO 2 reflector of 95% : 5%, the second blending paste with a ratio of 90% : 10%, and the third with a ratio of 85% : 15%. Each Paste blend then coated on conductive glass surface in dimensions of 1 cm x 1 cm. The dye solar cells which were resulted from the fabrication process then measured using I-V measurement system and a Sun Simulator to determine the current, voltage and resulted efficiency. Photoelectrode layers were then also measured by the UV - Visible absorbance to determine the characteristics of the light absorbance. We have also made measurements using SEM (scanning electron microscope) tools to investigate the surface characteristics of blending pastes of both paste types that have been used. The measurement results show that the DSSC resulted from blending paste with a ratio of 85% TiO 2 nanoparticle paste to 15% TiO 2 reflector paste has the greatest TiO 2 particle size and produces the greatest efficiency. Keywords: dye sensitized solar cell, TiO 2 reflector paste, scattering layer, TiO 2 nanoparticles paste. I. PENDAHULUAN Kebutuhan akan adanya energi baru sebagai alternatif sangat dibutuhkan, terutama sebagai energi pengganti yang terbarukan. Pada penelitian dye-sensitized solar cell (DSSC) telah banyak dipelajari dan dihasilkan beberapa teknik dan paduan bahan baik bahan dari alam maupun dari hasil rekayasa ilmiah. Dari beberapa pabrikasi yang telah dilakukan didapatkan hasil yang bervariasi bergantung pada bahan dan analisa yang digunakan [1]. Bahan utama pembuatan DSSC adalah material semikonduktor TiO 2 , karena material ini yang dapat menghasilkan efisiensi paling tinggi. Penggunaan partikel TiO 2 yang lebih besar sebagai pusat hamburan dicampur dalam matriks TiO 2 yang mengandung 20-50 nm partikel menyebabkan meningkatnya hamburan cahaya dalam lapisan TiO 2 dan secara keseluruhan meningkatkan efisiensi DSSC [2]. Dalam penelitian ini, kami akan meneliti pengaruh penggunaan pasta TiO 2 yang partikelnya lebih besar sebagai pusat hamburan dalam lapisan pasta TiO 2 yang dicampurkan dengan pasta TiO 2 partikel nano. * Corresponding Author. Email: lilisretna@gmail.com Received: July 17, 2014; Revised: August 26, 2014 Accepted: August 26, 2014 Published: December 30, 2014  2014 PPET - LIPI All rights reserved