19 Sintesis Bahan Absorber Gelombang Mikro Ni (1,5-x) La x Fe 1,5 O 4 dengan Metode Sol Gel (Yunasfi) SINTESIS BAHAN ABSORBER GELOMBANG MIKRO Ni (1,5-x) La x Fe 1,5 O 4 DENGAN METODE SOL GEL Yunasfi, Mashadi dan Ade Mulyawan Pusat Sains dan Teknologi Bahan Maju (PSTBM) - BATAN Kawaasan Puspiptek, Serpong 15314, Tangerang Selatan, Indonesia E-mail : yunasfi@gmail.com Diterima: 17 November 2016 Diperbaiki: 9 Juni 2017 Disetujui: 16 Juni 2017 ABSTRAK SINTESIS BAHAN ABSORBER GELOMBANG MIKRO Ni (1,5-x) La x Fe 1,5 O 4 DENGAN METODE SOL GEL. Telah dilakukan sintesis bahan absorber gelombang mikro Ni (1,5-x) La x Fe 1,5 O 4 dengan (x = 0,0 ; 0,5 dan 1,0) menggunakan metode sol-gel. Bahan Ni (1,5-x) La x Fe 1,5 O 4 disintesis dari campuran serbuk Ni(NO 3 ) 2 , Fe(NO 3 ) 3 dan La(NO 3 ) 3 dalam perbandingan mol masing-masing serbuk dengan menggunakan metode sol gel dan kemudian disinter pada suhu 1200 C selama 3 jam. Identifikasi fasa dengan X-Ray Diffractometer (XRD) menunjukkan bahwa dengan penambahan kandungan ion La 3+ terbentuk Ni (1,5-x) La x Fe 1.5 O 4 dengan 2 fasa yaitu NiFe 2 O 4 dan LaFeO 3 . Pengamatan morfologi dengan Scanning Electron Microscope (SEM) menunjukkan terbentuknya partikel yang tidak homogen yang artinya bahwa reaksi pembentukan Ni (1,5-x) La x Fe 1,5 O 4 belum sempurna. Sifat magnet sampel yang dianalisis dengan Vibrating Sample Magnetometer (VSM) menunjukkan bahwa sampel berperilaku feromagnetik, dimana nilai M s semakin rendah (pada rentang 32,76 emu/g hingga 9,40 emu/g) dan nilai H c semakin besar (pada rentang 200 - 247 Oe) seiring dengan penambahan kandungan La. Sedangkan kemampuan penyerapan gelombang mikro yang diukur dengan Vector Network Analyzer (VNA) menunjukkan nilai Reflection Loss (RL) maksimum diperoleh pada komposisi sampel x = 0,5 sebesar -27,5 dB pada frekuensi 10,60 GHz. Berarti bahwa NiLa 0,5 Fe 1,5 O 4 mampu menyerap gelombang mikro sebesar ~96 % pada frekuensi 10,60 GHz. Kata kunci: Nikel lantanum ferit, Metode sol-gel, Sifat magnet, Serapan gelombang mikro ABSTRAK SYNTHESIS OF Ni (1.5-x) La x Fe 1.5 O 4 AS MICROWAVE ABSORBER MATERIAL BY SOL GEL METHODS. Synthesis of Ni (1.5-x) La x Fe 1.5 O 4 with (x = 0, 0.5 and 1.0) as microwave absorber material by using sol-gel method have been carried out. The materials of Ni (1.5-x) La x Fe 1.5 O 4 powder are made from a mixture of Ni(NO 3 ) 2 , Fe(NO 3 ) 3 and La(NO 3 ) 3 in a mole ratio sol gel method and then sintered at 1200 °C for 3 hours. Phase identification by X-Ray Diffractometer (XRD) shows that the La addition have formed of two phases of NiFe 2 O 4 and LaFeO 3 . Morphological observation by Scanning Electron Microscope (SEM) shows unhomogenous particles which means the reaction in the formation of Ni (1.5-x) La x Fe 1.5 O 4 has not been perfect. Magnetic properties of samples were analyzed by vibrating sample magnetometer (VSM) shows ferromagnetic behaviour, where the M s value decrease (around of 32.76 to 9.40 emu/g) and value of H c increased (around of 200-247 Oe) along with the addition of the La content. While the ability of microwaves absorption measured by using Vector Network Analyzer (VNA) indicates that the maximum value of Reflection Loss (RL) obtained at the composition of x = 0.5 up to -27.5 dB at a frequency of 10.60 GHz. It means the Ni (1.5-x) La x Fe 1.5 O 4 composition is able to absorb microwave up to ~ 96% at a frequency of 10.60 GHz. Keywords: Nickle lanthanum ferrite, Sol-gel, Magnetic properties, Microwave absorber PENDAHULUAN Dalam beberapa tahun terakhir ini, telah banyak penelitian yang difokuskan pada sintesis nanometal oksida karena sifat optik, listrik dan magnetiknya yang luar biasa dibandingkan dengan senyawa dalam bentuk bulk dan salah satunya adalah ferit spinel, MFe 2 O 4 (M adalah ion logam valensi dua) [1]. Ferit spinel memiliki