The Journal of Engineering and Exact Sciences - JCEC ISSN: 2527-1075 Vol. 03 N. 08 (2017) 1106-1113 doi: 10.18540/jcecvl3iss8pp1106-1113 OPEN ACCESS CARACTERIZAÇÃO DO COMPORTAMENTO DE OXIDAÇÃO DE UMA LIGA INOXIDÁVEL Fe-Mn-Si-Cr-Ni-Co COM EFEITO DE MEMÓRIA DE FORMA EM ELEVADA TEMPERATURA CHARACTERIZATION ON OXIDATION BEHAVIOR OF A STAINLESS Fe-Mn-Si- Cr-Ni-Co SHAPE MEMORY ALLOY AT HIGH TEMPERATURE C. ARANA 1 , R. SILVA 2 , C. A. DELLA ROVERE 3 1 Universidade Federal de São Carlos, Departamento de Engenharia de Materiais, Brasil 2 Universidade Federal de São Carlos, Departamento de Engenharia de Materiais, Brasil 3 Universidade Federal de São Carlos, Departamento de Engenharia de Materiais, Brasil E-mail: arana.camila@hotmail.com RESUMO: Os aços inoxidáveis austeníticos com alto teor de Mn e baixo teor de Ni têm atraído muita atenção recentemente. Estas ligas, além de possuírem boas propriedades mecânicas e resistência à corrosão, possuem memória de forma. No entanto, o desenvolvimento destas ligas ainda é relativamente recente, e muitas de suas propriedades precisam ser estudadas. Deste modo, o objetivo deste trabalho foi caracterizar o comportamento de oxidação de uma liga Fe-Mn-Si-Cr-Ni-Co com memória de forma em 800 °C ao ar. Os resultados obtidos mostram que o comportamento de oxidação do material estudado obedece a uma lei parabólica. Após 120 h de oxidação, a camada de óxido formada na superfície da liga é composta principalmente de óxidos de Mn. A oxidação da liga provoca a transformação de fase de austenita para ferrita em regiões empobrecidas em Mn. ABSTRACT: Austenitic stainless steels with high Mn content and low Ni content have been attracting much attention recently. These alloys, besides having good mechanical properties and corrosion resistance, also present shape memory effect. However, the development of alloys of this kind is still very recent, and further studies on its properties are needed. Thus, the aim of this work was to characterize the oxidation behavior of a Fe-Mn-Si-Cr-Ni-Co shape memory alloy at 800 °C in air. The obtained results showed that the oxidation behavior of the studied material obeys a parabolic law. After 120 h of oxidation, the oxide layer formed on the surface of the alloy is composed mainly by Mn oxides. The oxidation of the alloy causes phase transformation of austenite to ferrite in Mn-depleted regions. 1. INTRODUÇÃO Os aços inoxidáveis austeníticos são materiais estruturais de engenharia extremamente importantes, pois combinam boas propriedades mecânicas, soldabilidade e excelente resistência à corrosão e ao calor. Estes aços são amplamente utilizados na produção de article info Article history: Received 2017-09-04 Accepted 2017-11-20 Available online 2017-12-20 PALAVRAS-CHAVE: Aço Inox Austenítico; Oxidação; EMF. KEYWORDS: Austenitic Stainless Steel; Oxidation; SME.