9 Studi Electrochemical Impedance Spectroscopy dari Lembaran Polyvinyl Alcohol dengan Penambahan LiClO 4 Sebagai Bahan Elektolit Baterai Li-Ion (Indra Gunawan) STUDI ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY DARI LEMBARAN POLYVINYL ALCOHOL DENGAN PENAMBAHAN LiClO 4 SEBAGAI BAHAN ELEKTOLIT BATERAI Li-ION Indra Gunawan, Wahyudianingsih dan Sudaryanto Pusat Sains dan Teknologi Bahan Maju - BATAN Kawasan Puspiptek, Serpong, Tangerang Selatan 15310 E-mail: irgun.IG@gmail.com Diterima: 5 Februari 2016 Diperbaiki: 24 Juni 2016 Disetujui: 26 September 2016 ABSTRAK STUDI ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY DARI LEMBARAN POLYVINYLALCOHOL DENGAN PENAMBAHAN LiClO 4 SEBAGAI BAHAN ELEKTOLIT BATERAI Li-ION. Telah disintesis bahan polimer elektolit padat untuk baterai Li ion, yaitu Polyvinyl Alcohol (PVA) dengan penambahan garam Lithium Perchlorate (LiClO 4 ) dengan berbagai konsentrasi. Studi Electrochemical Impedance Spectroscopy (EIS) dari bahan ini dilakukan dengan membuat plot Nyquist dari pengukuran dengan LCR meter. Bahan elektrolit ini disiapkan dengan cara serbuk PVA dilarutkan ke dalam aquadest dan ditambahkan garam LiClO 4 yang divariasi 0 %berat, 5 %berat, 10 %berat, 15 %berat, 20 %berat dan 25 %berat. Setelah proses pengeringan larutan, diperoleh lembaran PVA dengan penambahan garam LiClO 4 sebagai bahan elektrolit baterai Li ion. Plot Nyquist untuk lembaran PVA yang ditambahkan garam LiClO 4 yang divariasi 0 %berat, 5 %berat, 10 %berat, 15 %berat, 20 %berat dan 25 %berat telah dianalisis. Informasi resistensi elektrolit, ketahanan permukaan film dan resistensi transfer muatan diperoleh dengan pemodelan sirkuit yang setara sesuai dengan plot Nyquist. Hasil penelitian ini menunjukkan bahwa semakin tinggi kandungan LiClO 4 didalam PVA semakin besar pula difusi ion lithium di dalam lembaran bahan elektrolit. Kata kunci: Bahan elektrolit, Polyvinyl Alcohol, LiClO 4 , Baterai Li-ion ABSTRACT ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY STUDY OF POLYVINYLALCOHOL SHEET WITH ADDITION OF LiClO 4 AS ELECTROLYTE MATERIALOFLi-ION BATTERAY. Solid polymer electrolyte materials for Li ion battery have been prepared using polyvinyl alcohol (PVA) added by lithium perchlorate (LiClO 4 ) salt with various concentration. Electrochemical Impedance Spectroscopy (EIS) study of the material was done by making a Nyquist plot of the measurement with a LCR meter. These electrolyte materials prepared by using PVA powder which was dissolved into distilled water and added LiClO 4 salt varied in 0, 5, 10, 15, 20 and 25 w/w % . After drying the solution, PVA sheet with various LiClO 4 salt as Li ion battery electrolyte material was obtained. Nyquist plots for sheet of PVA with various LiClO 4 salt which varied 0, 5, 10, 15, 20 and 25 w/w% has been studied using LCR meter. Information of electrolyte resistance, resistance of the film surface and the charge transfer resistance is obtained by modeling the equivalent circuit according to the Nyquist plot. The result shows that the lithium ion diffusion increased with the increasing LiClO 4 content in the PVA film. Keywords: Electrolyte materials, Polyvinyl Alcohol, LiClO 4 , Li-ion battery PENDAHULUAN Aplikasi baterai lithium-ion disamping sebagai sumber daya untuk perangkat elektronik portabel, juga sedang dipertimbangkan sebagai kandidat yang menjanjikan untuk digunakan dalam Electric Vehicles