1295 § E-mail address: amcdonald@nickel.laurentian.ca ¶ Present address: 2031 Delmar Drive, Ottawa, Ontario K1H 5P6, Canada. The Canadian Mineralogist Vol. 39, pp. 1295-1306 (2001) NATROLEMOYNITE, A NEW HYDRATED SODIUM ZIRCONOSILICATE FROM MONT SAINT-HILAIRE, QUEBEC: DESCRIPTION AND STRUCTURE DETERMINATION ANDREW M. McDONALD § Department of Earth Sciences, Laurentian University, Sudbury, Ontario P3E 2C6, Canada GEORGE Y. CHAO ¶ Ottawa–Carleton Geoscience Centre, Department of Earth Sciences, Carleton University, Ottawa, Ontario K1S 5B6, Canada ABSTRACT Natrolemoynite is a new member of the lemoynite group found in altered or unaltered pegmatites cutting nepheline syenite at the Poudrette quarry, Mont Saint-Hilaire, Quebec. In altered pegmatites, it is associated with microcline, lemoynite, lepidocrocite, galena, sphalerite, calcite and pyrite, and in unaltered pegmatites, with biotite, microcline, albite, magnetite, a chlorite-group mineral, a burbankite-group mineral, an unidentified donnayite-(Y)-like mineral, zircon and pyrochlore. Crystals are colorless to white (occasionally with a slightly pink to red tinge), bladed to prismatic, elongate along [001], with maximum widths of 1 mm and lengths of 2 mm. The mineral typically develops in compact radial aggregates and spheres 4 mm in maximum diameter. It is transparent to translucent, with a vitreous to subadamantine luster and a white streak. The Mohs hardness is 3. Perfect {100} and {010} cleavages and a poor {001} cleavage are observed. D meas is 2.47(1) g/cm 3 and D calc , 2.50 g/cm 3 . Natrolemoynite is biaxial negative,  1.533(1),  1.559(1),  1.567(1), 2V meas. = 63(1)°, 2V calc. = 57(1)°; dispersion is weak, with r and v crossed. The optical orientation is X = b, Z  a = 41° (measured in the obtuse angle ). The average result of nineteen electron-microprobe analyses gave Na 2 O 7.47, K 2 O 1.29, CaO 0.37, MnO 0.12, Al 2 O 3 0.04, SiO 2 54.51, TiO 2 0.38, ZrO 2 21.97, Nb 2 O 5 1.01 and H 2 O (calc.) 14.72, total 101.88 wt.%, corresponding to (Na 2.66 K 0.30 Ca 0.07 Mn 0.02 ) 3.05 (Zr 1.96 Nb 0.08 Ti 0.05 ) 2.09 (Si 9.99 Al 0.01 ) 10 O 25.79 • 9H 2 O on the basis of 10(Si + Al) or, ideally, Na 4 Zr 2 Si 10 O 26 •9H 2 O. It is monoclinic, C2/m, a 10.5150(2), b 16.2534(4), c 9.1029(3) Å,  105.462(2)°, V 1499.4(1) Å 3 , Z = 2. The structure was refined to R = 4.2% for 2133 reflections [F o > 4(F o )]. Six-membered rings of SiO 4 tetrahedra are linked along [001] by ZrO 6 octahedra to form a zirconosilicate framework. Channels parallel to [001] are occupied by Na and H 2 O. Evidence is provided for limited Na ↔ H 3 O + substitution. Crystal-chemical and field relations indicate that paragenetically, natrolemoynite is one of the last sodium zirconosilicate hydrate phases to develop. Keywords: natrolemoynite, new mineral species, zirconosilicate, crystal structure, Mont Saint-Hilaire, Quebec. SOMMAIRE La natrolemoynite est un nouveau membre du groupe de la lemoynite, découverte dans des pegmatites altérées ou non recoupant des syénites néphéliniques dans la carrière Poudrette, au mont Saint-Hilaire, Québec. Dans le cas des pegmatites altérées, elle est associée à microcline, lemoynite, lepidocrocite, galène, sphalérite, calcite et pyrite; lui sont associés dans les pegmatites non altérées biotite, microcline, albite, magnétite, un minéral du groupe de la chlorite, un autre du groupe de la burbankite, un minéral non identifié ressemblant à la donnayite-(Y), zircon et pyrochlore. Les cristaux sont incolores à blanc (possiblement avec une teinte rosâtre ou rougeâtre), en lames ou en prismes, allongés selon [001], avec une largeur et une longueur maximales de 1 et 2 mm, respectivement. Le minéral se présente en amas compacts fibroradiés et en boules atteignant un diamètre de 4 mm. La natrolemoynite est transparente à translucide, avec un éclat vitreux ou sub-adamantin et une rayure blanche. La dureté de Mohs est 3. Les clivages {100} et {010} sont parfaits, et le clivage {001}, de piètre qualité. La densité mesurée est 2.47(1) g/cm 3 , et la densité calculée, 2.50 g/cm 3 . La natrolemoynite est biaxe négative,  1.533(1),  1.559(1),  1.567(1), 2V mes. = 63(1)°, 2V calc. = 57(1)°; la dispersion est faible, avec r et v croisés. L’orientation optique est X = b, Z  a = 41° (mesuré dans l’angle  obtus). La moyenne des résultats de dix-neuf analyses à la microsonde électronique a donné Na 2 O 7.47, K 2 O 1.29, CaO 0.37, MnO 0.12, Al 2 O 3 0.04, SiO 2 54.51, TiO 2 0.38, ZrO 2 21.97, Nb 2 O 5 1.01 et H 2 O (calc.) 14.72, pour un total de 101.88% (poids), ce qui correspond à (Na 2.66 K 0.30 Ca 0.07 Mn 0.02 ) 3.05 (Zr 1.96 Nb 0.08 Ti 0.05 ) 2.09 (Si 9.99 Al 0.01 ) 10 O 25.79 •9H 2 O sur une base de 10(Si + Al) ou, idéalement, Na 4 Zr 2 Si 10 O 26 •9H 2 O. Elle est monoclinique, C2/m, a 10.5150(2), b 16.2534(4), c 9.1029(3) Å,  105.462(2)°, V 1499.4(1) Å 3 , Z = 2. La structure a été affinée jusqu’à un résidu R de 4.2% avec 2133 réflexions