http://www.revistadechimie.ro REV.CHIM.(Bucharest)♦69♦No.12♦2018 The Influence of Zr on Microstructure, Mechanical Properties and Corrosion Resistance in Mg-Y-Zr Biodegradable Alloys STEFAN LUPESCU¹ , CORNELIU MUNTEANU¹ , BOGDAN ISTRATE¹ *, KAMEL EARAR 2 1 Gheorghe Asachi University of Iasi, Mechanical Engineering Department, 6 D. Mangeron Blvd, 700050, Iasi, Romania 2 Dunarea de Jos University of Galati, Faculty of Medicine, Dental Medicine, Al. I. Cuza 35 Str., 800010, Galati, Romania The latest magnesium alloys are widely used in the medical field, especially for biodegradable implants. Magnesium alloys are very attractive for applications in different structures in the automotive, aerospace, printing and even medical fields [1]. It should be noted that some magnesium alloys have excellent damping properties as well as good mechanical properties, making them promising to respond to high damping needs for vibration control [1,2]. Although widely used, magnesium has a low corrosion resistance. To improve this resistance, different types of magnesium based on aluminum, such as Ca, Mn, Zn, Zr, Si and rare rare (Y , Gd ..), can be developed. The main purpose of this paper is to investigate the properties of a primary alloy based on the Mg-1Y-0,5Zr system with different concentrations of Zr (0.5,1,2) used in the development of alloys based on the biodegradability of Mg. Surface morphology was characterized by electronic scanning microscopy (SEM), X-ray diffraction (XRD) and optical microscopy. After XRD analysis, it was observed that certain specific compounds were made up of Mg2Ca, MgZr, Mg2Y , Mg24Y5 having the main Mg formed in the hexagonal structure, but Mg24Y5 are the cubic crystalline structure. Also, the microhardness of the alloy is higher than pure Mg and the scratch mark is smaller than that of pure Mg. The corrosion resistance was developed using linear voltammetry in specific medium and corrosion showed that it had significantly decreased for masteralloy. As a final conclusion, the structural properties of this model are recommended for use as medical implants. Keywords: Micro-Hardness, SEM, XRD, optical microstructure *email:bogdan_istrate1@yahoo.com Mg alloys have gained a lot of interest over the past few years in various fields such as automotive, medical, aerospace industries due to their low density, good casting capacity and higher specific strength. [1, 4] For medical implants, it has been shown that Mg is a modulus of elasticity comparable to that of the cortical bone, eliminating the stress protection elements that may occur due to a impediment of a module between the implanted material and the bone. [2] Mg-based implants have been shown to have a better osteointegration at the bone-implant interface compared to Ti-based alloys. [3] In addition to these significant advantages, it has also been shown to be disadvantages by low strength and high rate of degradation, which are major obstacles to the use of Mg in medical applications, as they can lead to the loss of structural integrity and the elimination of toxic substances before the tissue is fully cured [18]. Similarly, although Li has been used in medicine for nearly 150 years [16, 17], it has not been widely used in implanted materials where a continuous exposure of mg per day can occur [18]. In over the last decade significant research has been carried out on Mg-based alloys to eliminate as many disadvantages as possible. Pure Mg is unable to provide the necessary mechanical properties [13, 14] and corrosion resistance [15] required for a wide variety of implant applications. Therefore, potential alloying elements should be carefully considered. Alloying Mg with various elements such as Al, Zn, Ca, RE, and others has been proven to improve mechanical properties and reduce the rate of degradation of Mg. [6-12] The addition of Y (Yttrium) has been used in Mg alloys for biodegradable applications due to its beneficial effect on corrosion and resistance of Mg alloys as well as the lack of toxicity at normal alloying concentration. [7, 8] It is demonstrated that Y2O3 has high thermodynamic stability and has been shown to reduce the rate of degradation of Mg-based alloys. [7-9] Zr also reduces the rate of degradation over time. Based on these considerations, this paper seeks to investigate the mechanical properties of the Mg-Zr-Y alloy with different concentrations of Zr (0.5, 1, 2) to make a comparison between the properties of the 3 recipes and decide which one is the most indicated for medical applications. Experimental part Materials and methods Alloys based on Mg: B1(Mg-1Y-0.5Zr), B2(Mg-1Y-1Zr), B3(Mg-1Y-2Zr) were prepared in molds of graphite crucibles and homogenized at 700 degrees Celsius for 3 hours in an induction furnace under the protection of an inert atmosphere (Ar). This operation was repeated in all three samples. Samples were cut to sizes 7-8mm x 10mm, polished primarily with abrasive paper with grains of 150 to 1000 SiC, then cleaned with pure ethanol and dried in free air before being worked out. After elaboration, the ingots were cut into pills with a diameter of about 15 mm and a thickness of 5 mm. The samples were sanded with abrasive paper with a grain size of up to 2000 SiC to obtain a uniform surface. The analyzed surface of each sample was milled and polished to a final finish with a 0.05μm alumina suspension. Prior to observation, the samples were etched using 4% w / w nitric acid in ethanol for 5-8 s, thoroughly washed with water and alcohol and then dried with hot air. The morphology and alloy microstructure was determined using a double BSD (backscatter) LFD (double field detector) with a SEM Quanta 200 3D DUAL BEAM electronic scanning microscope. For phase analysis, XRD analysis was 3382