Ariyani, dkk: Pengaruh komposisi beberapa ... 13 ARTIKEL PENELITIAN Pengaruh komposisi beberapa glass ber non dental terhadap kelarutan komponen ber reinforced composites Ariyani Faizah*, Widjijono**, Nuryono*** *Fakultas Kedokteran Gigi, Universitas Muhammadiyah Surakarta, Surakarta, Jawa Tengah, Indonesia **Departemen Biomaterial, Fakultas Kedokteran Gigi, Universitas Gadjah Mada, Yogyakarta, Indonesia ***Departemen Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Gadjah Mada, Yogyakarta, Indonesia *Jl Kebangkitan Nasional No 101 Penumping, Surakarta, Jawa Tengah, Indonesia; e-mail: ariyani_faizah@yahoo.com ABSTRAK E glass ber dental adalah ber yang sering digunakan di kedokteran gigi. Ketersediaan E glass ber di Indonesia masih sangat terbatas. Berbagai jenis bahan glass ber non dental banyak ditemukan dipasaran sebagai material engeenering dengan harga yang relatif murah sehingga diharapkan dapat digunakan sebagai alternatif pengganti E glass ber dental. Komposisi glass ber non dental hampir sama dengan E glass ber dental. Komposisi berpengaruh terhadap sifat mekanis dan sifat-sifat kimia ber. Komposisi glass ber seperti Na 2 O dan K 2 O akan meningkatkan ketahanan terhadapap air. Tujuan dari penelitian ini adalah mengetahui pengaruh komposisi glass ber non dental terhadap kelarutan komponen. Bahan yang digunakan dalam penelitian ini adalah E glass ber dental (Fiber-splint, Polydentia SA, Switzerland), glass ber non dental komposisi A (LT, China), komposisi B (CMAX, China), komposisi C (HJ, China), owable komposit (CharmFill Flow, Denkist, Korea) dan silane coupling agent (Monobond S, Ivoclar Vivadent, Liechtenstein). Subjek dibagi dalam 4 kelompok untuk dilakukan uji kelarutan berdasarkan ISO 4049. Hasil yang diperoleh dianalisis menggunakan ANAVA satu jalur (α = 0,05). Hasil penelitian menunjukkan rerata kelarutan komponen (%) yang terendah pada kelompok E-glass ber dental (0,476±0,03) dan hasil tertinggi pada glass ber non dental C (0,600±0,01). Hasil uji Anava satu jalur menunjukkan perbedaan yang bermakna antara komposisi ber pada kelarutan komponen (p<0,05). Kesimpulan penelitian adalah komposisi Na 2 O dan K 2 O serta CaO dan MgO yang rendah dapat menurunkan sifat kelarutan komponen dari ber reinforced composites. Kata kunci: glass ber non dental, kelarutan komponen, komposisi ber ABSTRACT: The effect of composition glass ber non dental on water solubility of ber reinforced composites. E glass ber dental is one of the most used dental bers in several applications in the dental eld. However, the available of E glass ber dental in Indonesia is very limited. A variety of types of non-dental glass ber material is easily found as the materials engineering. The purpose of the study was to evaluate the effect of composition non dental glass ber on the component solubility of FRC. The materials used in the research was E glass ber dental (Fiber splint, Polydentia SA, Switzerland), composition A non-dental glass ber (LT, China), composition B (CMAX, China), composition C (HJ, China), owable composite (Charmll Flow, Denkist, Korea) and silane coupling agent (Monobond S, Ivoclair Vivadent, Liechtenstein). The subject was divided into 4 groups. Component solubility test was based on the ISO 4049. The result was then analyzed with one way ANOVA (α=0,05). The result of the research showed that on the average percentage of the solubility (%), the lowest was on the group of E glass ber dental (0.476±0.03) and the highest was on the non dental glass ber C (0.600±0.01). The result of the one way ANOVA test showed a signicant difference between the compositiom ber on the component solubility. The conclusion the research was that low content of Na2O K2O, CaO and MgO decreased the component solubility of FRC. Keywords: ber glass non dental, component solubility, ber composition PENDAHULUAN Kehilangan gigi geligi memiliki konsekuensi sosial, psikologis dan emosional sehingga mengurangi kualitas hidup seseorang. 1,2 Pada kasus kehilangan satu gigi, pilihan perawatan yang biasa dilakukan adalah dengan pemakaian gigi tiruan cekat. Salah satu bahan pilihan pembuatan gigi tiruan cekat adalah porcelain fused to metal (PFM). Pema- kaian PFM terlihat natural dan mempunyai waktu pemakaian yang cukup panjang dan estetika yang cukup baik 3 tetapi PFM memiliki beberapa kelemahan diantaranya adalah efek toksik dari logam yang digunakan, membutuhkan beberapa kali kunjungan, biaya yang lebih tinggi, 4 membutuhkan preparasi gigi abutment yang cukup luas dan pengerjaan laboratorium yang rumit. 5 Teknik inovatif bahan kedokteran gigi membawa perkembangan dalam perawatan. Dua hal yang menjadi fokus pada Majalah Kedokteran Gigi Indonesia Vol 2 No 1 – April 2016 p-ISSN 2460-0164, e-ISSN 2442-2576 http://jurnal.ugm.ac.id/mkgi DOI: 10.22146/majkedgiind.11249