Jurnal Pendidikan Fisika dan Keilmuan (JPFK) Vol. 6, No 1. , Maret 2020, pp. XX-XX P-ISSN: 2442-8868, E-ISSN: 2442-904X, DOI: https://doi.org/10.25273/jpfk.v6i1.5236 Received Oktober 10, 2019; Revised November 26, 2019; Accepted Maret 19, 2020 Kurva Histeresis Bahan Feromagnetik Co0.8Pt0.2 pada Tiga Daerah Domain Irmawati Hasanah 1 , Lutfi Rohman 1 , Edy Supripyanto 1 1 Jurusan Fisika, FMIPA, Universitas Jember, Jember 68121, Jawa Timur, Indonesia e-mail: irmawatihasanah10031997@gmail.com Abstrak Bahan magnetik alloy Co0.8Pt0.2, merupakan bahan yang mempunyai konstanta anisotropi dan tahanan korosi yang tinggi sehingga bisa dijadikan pembuatan hardisk dengan kapasitas penyimpanan yang besar pada ukuran nanometer. Ukuran kritis bahan CoPt dianalisis dengan grafik hubungan rapat energi dengan ukuran sisi kubus yang terdapat tiga zona domain, yakni single domain, transisi dan multi domain. Nilai ukuran kritis yang dihasilkan sebesar 20 nm, nilai tersebut dilihat dari titik akhir dari zona single domain yang akan menuju ke zona transisi. Kurva histerisis bahan CoPt ini menghasilkan medan koersivitas yang kecil yaitu seperti halnya magnet dalam golongan soft magnet. Penelitian ini mengkaji sifat magnetik bahan CoPt dalam bentuk nanocube menggunakan kurva histerisis dan ukuran kritis yang dikaji dalam bentuk grafik hubungan rapat energi (KJ/m3) dengan ukuran sisi kubus (nm) yang dilakukan dengan memvariasikan ukuran bahan. Ukuran kritis dapat ditinjau dengan membaginya dalam tiga zona yakni single domain, transisi dan multi domain. Nilai ukuran kritis bahan sebesar 20 nm. Kurva histerisis pada zona single domain dengan sisi kubus 8 nm medan koersivitas bernilai 3,46×10- 7 T, pada zona transisi 20 nm medan koersivitas yang dihasilkan sebesar 9,43×10-7 T sedangkan pada multi domain 29 nm medan koersivitas yang dihasilkan bernilai 1,5×10-6 T. Kata Kunci: CoPt, Ukuran Kritis, Kurva histerisis, nanocube, magnetisasi saturasi. Hysteresis Curves of Co0.8Pt0.2 Ferromagnetic Material in Three Domain Regions Abstract The magnetic alloy material Co0.8Pt0.2, is a material that has a high anisotropy constant and corrosion resistance so that it can be made into a hard disk with a large storage capacity at nanometer size. The critical size of CoPt material is analyzed by the graph of the relationship of energy density with the size of the side of the cube which has three domain zones, namely single domain, transition and multi domain. The resulting critical size value is 20 nm, the value is seen from the endpoint of the single domain zone that will go to the transition zone. The hysteresis curve of the CoPt material produces a small coercivity field that is like a magnet in the soft magnet group. This study examines the magnetic properties of CoPt material in the form of nanocubes using hysteresis curves and critical sizes which are examined in the form of a graph of the relationship of energy density (KJ / m3) with the size of the side of the cube (nm) which is done by varying the size of the material. Critical measures can be reviewed by dividing them into three zones namely single domain, transition and multi domain. The critical size value of the material is 20 nm. The hysteresis curve in a single domain zone with an 8 nm cube side of the coercivity field was 3,46×10-7 T, in the 20 nm transition zone the resulting coercivity field was 9,43×10-7 T while in the multi domain 29 nm the resulting coercivity field was worth 1,5×10- 6. Keywords: CoPt, Critical Size, Hysteresis Curve, nanocube, saturation magnetization How to Cite: H, Irmawati., R, Lutfi., S, Edy. (2020). Kurva Histeresis Bahan Feromagnetik Co0.8Pt0.2 pada Tiga Daerah Domain. Jurnal Pendidikan Fisika dan Keilmuan (JPFK), 6(1), 47- 54. doi: https://doi.org/10.25273/jpfk.v6i1.5236