Acta metall, mater. Vol. 42, No. 11, pp. 3615-3627, 1994 Copyright © 1994 Elsevier Science Ltd Pergamon 0956-7151(94)E0175-G Printed in Great Britain. All rights reserved 0956-7151/94 $7.00 + 0.00 EFFECT OF AUSTENITE PANCAKING ON TEXTURE FORMATION IN A PLAIN CARBON AND A Nb MICROALLOYED STEEL M. P. BUTRON-GUILLi~N, J. J. JONAS and R. K. RAYt Department of Metallurgical Engineering, McGill University, 3450 University Street, Montreal, Canada H3A 2A7 (Received 20 December 1993; in revised form 20 March 1994) Abstract--The way in which texture development is affected by austenite pancaking was studied in a plain carbon and a niobium steel. Three processing parameters (austenitizing temperature, finish rolling temperature and amount of reduction) were varied, and their influence on the state of the austenite was analyzed. It was found that the presence of niobium, which leads to pancaking of the austenite when low finishing temperatures are employed, strengthened the transformation products produced from the copper, brass, S and Goss orientations in the austenite. Larger reductions resulted in sharper textures, especially in the microalloyed steel. The effect of austenitizing temperature was not particularly strong. Several f.c.c. ideal orientations were transformed according to the Kurdjumov-Sachs relationship, and the b.c.c. products resulting from this analysis are compared with the experimental results. When recrystallized austenite transforms, it is shown that the cube component transforms preferentially into the {001}(110) rotated cube orientation, with lower than expected intensities displayed by the Goss and rotated Goss components. Similar trends are observed with respect to the four main deformation components; these tendencies are interpreted in terms of variant selection and selective growth. Rg~sumr----L'effet de l'rcrouissage de l'austrnite sur le drveloppement des textures de transformation a 6t6 6tudi6 pour un acier au carbone et un acier au niobium. Trois paramrtres d'oprration (temprrature d'austrnitisation, temprrature finale de laminage et rrduction) ont 6t6 varirs pour en drterminer l'influence sur l'rtat de l'austrnite. La prrsence de niobium, qui retarde la recristallisation de l'austrnite lorsque la temprrature de finition est suflisamment basse, renforci les produits de transformation obtenus des orientations cuivre, laiton, Set Goss dans l'austrnite. Un taux de laminage plus prononc6 renforci les textures, specialement dans les acier microallirs. L'effet de la temprrature d'austenitisation n'est pas particulidrement important. Plusieurs orientations idrales c.f.c, ont 6t6 transformres en employant la relation de Kurdjumov-Sachs. Les produits c.c. obtenus sont comparrs avec les rrsultats exprrimentaux. Lorsque l'austrnite recristallisre se transforme, l'orientation cube disparait de prrfrrence au profit du cube tourn6 autour de la direction normale {001 }(110), les autres produits de transformation Goss et Goss tourn6 de la direction normale possedant des intensitrs infrrieures ft. celles prrdites. Des tendances similaires sont observres aprrs transformation des quatre principales orientations de drforrnation; ces rgsultats sont expliqurs/t partir des mrcanismes de croissance srlective. Zusammenfassung--Die Art und Weise, in der die Texturentwicklung durch Austenit-"Pfannkuchen"-Bil- dung beeinfiuBt wird, wurde fiir einen einfachen Kohlenstoff- und einen Niob-Stahl untersucht. Drei ProzeBparameter (Austenitisierungstemperatur, Feinwalztemperatur und Grad der Reduktion) wurden variiert und ihr EinfluB auf den Zustand des Austenit wurden untersucht. Es wurde festgestellt, dab die Answesenheit von Niob, die bei geringen Walztemperaturen zur "Pfannkuchen"-Bildung des Austenites ffihrt, die von den Kupfer-, Messing-, S- und Goss-orientierungen im Austenit erzengten Transformation- sprodukte verst/irkt. GrrBere Walzgrade fiihrten zu sch/irferen Texturen, insbesondere im mikrolegierten Stahl. Der EinfluB der Austenitisierungstemperatur war nicht besonderes stark. Mehere ideale k.f.z. Orientierungen wurden nach der K-S-Beziehung transformiert und die k.r.z. Produkte, die aus dieser Analyse resultierten, wurden mit den experimentellen Resultaten verglichen. Es wird gezeigt, dab bei der Transformation yon re-kristallisiertem Austenit die Wiirfelkomponente bevorzugt in die {001 }(110) rotierte Wfirfelorientierung transformiert, w/ihrend die Goss- und rotierten Goss-Komponenten geringere Intensit/iten als erwartet hatten..~nliche Trends wurden bein den vier Hauptdeformationskomponenten beobachtet. Diese Tendenzen wurden vom Standpunkt eines selektiven Wachstumsmechanismus interpretiert. "t'Present address: Department of Metallurgical Engineering, Indian Institute of Technology, Kanpur 208016, India. 3615