Fakultas Teknik UNR, Gradien Vol.11, N0.1, April 2019 Fakultas Teknik UNR 46 ANALISIS LIMBAH BENDA UJI BETON UNTUK MENSUBSTITUSI AGREGAT KASAR PADA CAMPURAN BETON I Gusti Made Sudika 1) , I Gusti Ngurah Eka Partama 2) , I Gede Surya Dinata 3) E-mail : sudikagusti@yahoo.com 1) , epartama@gmail.com 2) , suryadinata896@gmail.com 3) Prodi Teknik Sipil Fakultas Teknik Universitas Ngurah Rai ABSTRAK Limbah benda uji beton setelah dilakukan pengujian selanjutnya ditumpuk dan dibuang. Untuk kapasitas yang besar akan menimbulkan masalah karena memerlukan areal penampungan yang luas dan jika langsung dibuang ke tanah akan mengurangi kesuburan tanah dan merusak ekosistem. Secara visual fisik material penyusun beton dan padatan limbah benda uji masih bagus dan diperlukan kajian agar bias dimanfaatkan kembali sebagai campuran beton. Penelitian ini dilakukan dengan membuat sampel benda uji dengan mutu beton rencanaf’c=22 MPa dengan variasi kandungan agregat kasar limbah benda uji beton sebanyak 0%, 25%, 50%, 75% dan 100% terhadap berat agregat kasar yang dibutuhkan.Rancangan campuran (mix design) beton mengunakan SNI 03–2834- 2000. Sampel benda uji dibuat berbentuk silinder berdiameter 15 cm dan tinggi 30 cm, disiapkan 3 buah sampel untuk setiap variasi campuran dan diuji pada umur 14 dan 28 hari. Semen portland yang digunakan adalah Tipe PCC Merk Tiga Roda dengan konposisi senyawa kimia mendekati Semen Tipe I. Agegrat kasar dan halus dari batuan alami Gunung Agung serta air bersih dari PDAM Kota Denpasar. Hasil penelitian menghasilkan kuat tekan tertinggi dicapai saat substitusi agregat limbah benda uji beton sebanyak 25% dari berat total agregat kasar yang diperlukan yaitu 25.76 MPa pada umur 14 hari dan 29.82 MPa pada umur 28 hari. Kuat tekan terendah ditunjukkan saat substitusi agregat limbah beton sebanyak 100%, dengan kuat tekan sebesar 22.36 dan 26.61 MPa masing-masing saat benda uji berumur 14 dan 28 hari. Hasil pengujian kuat tarik belah menunjukkan nilai tertinggi yang dicapai yaitu saat substitusi agregat limbah beton sebanyak 25% terhadap berat agregat kasar yang diperlukan, dimana saatbenda uji berumur 14 dan 28 hari, kuat tarik belah mencapai 2.57 dan 2.97 MPa. Nilai kuat tarik belah terendah ditunjukkan saat substitusi agregat limbah beton sebanyak 100% terhadap berat kebutuhan agregat kasar sebesar 2.24 dan 2.67 MPa untuk masing-masing benda uji berumur umur 14 dan 28 hari. Kata kunci : Limbah beton, Agregat , Kuat tekan, Kuat tarik belah. ABSTRACT The concrete test objects waste after testing are then stacked and disposed of. For large capacities it will cause problems because it requires a large holding area and if it is discharged directly to the ground it will reduce soil fertility and destroy the ecosystem. Visually the concrete constituent material and the solids of the test object waste are still good and studies are needed so that it can be reused as a concrete mixture. This research was carried out by making samples of specimens with concrete quality plan f'c = 22 MPa with variations in the content of coarse aggregate waste of concrete specimens as much as 0%, 25%, 50%, 75% and 100% of the weight of coarse aggregate needed. Concrete mix design using SNI 03-2828-2000. The sample specimens were made in the form of cylinders 15 cm in diameter and 30 cm high, prepared 3 samples for each variation of the mixture and tested at 14 and 28 days. The portland cement used is the Tiga Roda PCC Brand Type with a chemical compound exposition approaching Type I Cement. Coarse and fine aggregate from the Gunung Agung natural rock and clean water from PDAM Denpasar City The results of the study resulted in the highest compressive strength achieved when the substitution of concrete specimens as much as 25% of the total weight of coarse aggregate needed was 25.76 MPa at 14 days and 29.82 MPa at 28 days. The lowest compressive strength was shown when the concrete waste aggregate substitution was 100%, with compressive strength of 22.36 and 26.61 MPa, respectively when the specimens are 14 and 28 days old. The results of the tensile strength test showed the highest value achieved was when the concrete waste aggregate substitution of 25% of the weight of coarse aggregate is needed, where when the specimens are 14 and 28 days old, the tensile strength reaches 2.57 and 2.97 MPa. The lowest split tensile strength value was shown when the concrete waste aggregate substitution was 100% to the weight of the gross aggregate requirement of 2.24 and 2.67 MPa for each specimen aged 14 and 28 days, respectively. Key words:Concrete waste, aggregate, compressive strength, tensile strength. Dosen 1 , Dosen 2 , Mahasiswa 3