Jurnal Kimia dan Kemasan, 41(2), 55-64 , 2019 ©Author(s); http://dx.doi.org/10.24817/jkk.v41i2.5417 Pendekatan Teknologi Green Chemistry….......................................… Elsya et al. 55 PENDEKATAN GREEN SYNTHESIS NANOPARTIKEL CuFe 2 O 4 DENGAN BANTUAN EKSTRAK DAUN GAMBIR DAN SIFAT ANTI BAKTERINYA Suci Aulia Rahmi Elsya 1 , Zulhadjri 2 , dan Syukri Arief 2 1 Program Magister Kimia, Universitas Andalas Padang, Sumatera Barat 2 Laboratorium Kimia Material, Universitas Andalas Kampus Limau Manis, Padang, Sumatera barat E-mail : syukriarief@gmail.com Received : 29 Juli 2019; revised : 5 Agustus 2019; accepted : 22 Agustus 2019 ABSTRAK PENDEKATAN GREEN SYNTHESIS NANOPARTIKEL CuFe2O4 DENGAN BANTUAN EKSTRAK DAUN GAMBIR DAN SIFAT ANTI BAKTERINYA. Perkembangan nanoteknologi berkaitan dengan nanomaterial berfungsi untuk meningkatkan aktivitas antibakteri serta mengurangi pemakaian logam. Penelitian ini bertujuan untuk mengetahui pengaruh suhu, pH, dan waktu reaksi terhadap sifat nanopartikel tembaga ferit (CuFe2O4), yang selanjutnya diaplikasikan sebagai agen antibakteri. Nanopartikel Tembaga Ferit (NTF) disintesis dengan memadukan metode green sintesis dan hidrotermal menggunakanekstrak daun gambir (Uncaria gambir Roxb.) sebagai capping agent. Hasil analisis X-Ray Diffraction (XRD) memberikan informasi bahwa NTF yang disintesis dengan penambahan ekstrak daun gambir dan NaOH serta dengan penambahan NaOH saja pada pH 12 dan suhu 180 °C selama 8 jam menghasilkan NTF dengan struktur kubik berpusat muka dengan grup ruang Fd3mZ sesuai dengan standar ICSD #153013. NTF yang disintesis dengan penambahan ekstrak daun gambir dan NaOH pada pH 12 suhu 180 °C selama 8 jam memiliki ukuran paling kecil yaitu 24 nm. Berdasarkan hasil Scanning Electron Microscope (SEM), NTF yang disintesis dengan ekstrak daun gambir dan NaOH, serta NaOH saja pada suhu 180 °C selama 8 jam pada pH 12 berbentuk bulat dengan distribusi yang merata meskipun masih ada yang teraglomerasi. Nanopartikel tembaga ferit yang disintesis diaplikasikan pada bakteri gram positif (Staphilococcus aureus) dan gram negatif (Escherichia coli) menggunakan metode difusi sumuran. NTF yang disintesis pada suhu 180 °C selama 8 jam pH 10 dan pH 12 efektif menghambat pertumbuhan bakteri E. coli dan S. aureus. Kata kunci : Nanopartikel, Tembaga ferit, Green sintesis, Gambir ABSTRACT GREEN SYNTHESIS APPROACH OF CuFe2O4 NANOPARTICLES USING GAMBIR LEAF EXTRACT AND ITS ANTIBACTERIAL ACTIVITY. The development of nanotechnology-related to the nanomaterial is served to improve the antibacterial activity and reduce the use of metal. This study aims to investigate the effect of temperature, pH, and reaction time on the characteristic of copper ferrite nanoparticles (CuFe2O4), which were then applied as antibacterial agent. Copper ferrite nanoparticles (NTF) were synthesized by combining green synthesis and hydrothermal methods using gambir leaf extract (Uncaria gambir Roxb.) as a capping agent. The X-Ray Diffraction (XRD) analysis provided information that the NTF synthesized using the combination of gambir leaf extract and NaOH, and the addition of NaOH only at pH of 12 and temperature reaction of 180 °C for 8 hours resulting in a face center cubic structured of NTF with the space group of Fd3mZ related to ICSD #153013 standard. NTF synthesized using gambir leaf extract and NaOH at pH of 12 and temperature of 180 °C for 8 hours had the smallest size of 24 nm. Based on the Scanning Electron Microscope (SEM) photograph, it was found that NTF synthesized with combination of gambir leaf extract and NaOH, and NaOH only at 180 °C for 8 hours at pH of 12 were spherical in shape and well distributed, even though there was still agglomeration. The synthesized NTF was tested against gram positive (Staphylococcus aureus) and gram negative bacteria (Escherichia coli) using well diffusion method. NTF synthesized at 180 °C for 8 hours at pH 10 and pH of 12 were effective in inhibiting the growth of E. coli and S. aureus bacteria. Keywords : Nanoparticles, Copper ferrite, Green synthesis, Gambir