ADSORPSI SENG(II) OLEH BIOMASSA Azolla microphylla-SITRAT: KAJIAN DESORPSI MENGGUNAKAN LARUTAN ASAM NITRAT Mifta Fauziah Felayati, Danar Purwonugroho*, Mohammad Misbah Khunur Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Brawijaya Jl. Veteran Malang 65145 *Alamat korespondensi, Tel : +62-341-575838, Fax : +62-341-575835 Email: danar@ub.ac.id ABSTRAK Penelitian tentang desorpsi seng(II) dari biomassa Azolla microphylla diesterifikasi asam sitrat telah dilakukan. Tujuan penelitian ini adalah untuk menentukan kondisi optimum desorpsi seng(II) oleh biomassa Azolla microphylla diesterifikasi asam sitrat. Biomassa diesterifikasi dengan cara mencampurkan 5 g biomassa ke dalam 50 mL larutan asam sitrat 0,8 M dengan pemanasan 120°C selama 3,5 jam. Percobaan adsorpsi - desorpsi dilakukan menggunakan metode batch. Adsorpsi seng(II) 100 mg/L dilakukan pada pH 6 dengan waktu kontak 45 menit. Percobaan desorpsi dilakukan dengan cara mensuspensikan adsorben yang mengikat seng(II) ke dalam 25 mL larutan HNO 3 dengan variasi konsentrasi 0,1; 0,5; 1,0; 1,5 dan 2,0 M dan variasi waktu kontak 30; 45; 60; 75 dan 90 menit. Konsentrasi seng(II) yang terdesorpsi ke dalam larutan pendesorpsi ditentukan menggunakan spektrofotometer serapan atom. Hasil penelitian menunjukkan bahwa kondisi optimum desorpsi seng(II) terjadi pada penggunaan larutan HNO 3 1,0 M dan waktu kontak 60 menit memberikan persen desorpsi sebesar 93,62 %. Kata kunci: Azolla microphylla, batch, esterifikasi, seng(II) ABSTRACT Research about desorption of zinc(II) bound to Azolla microphylla biomass esterified by citric acid has done. The purpose of this study was to determine the optimum conditions for the desorption of zinc(II) by Azolla microphylla biomass esterified by citric acid. Biomass prepared by mixing 5 g of biomass into 50 mL of 0.8 M citric acid solution with heating 120°C for 3.5 hours. Experiment adsorption – desorption were performed using batch method. Adsorption of zinc(II) 100 mg/L performed at pH 6 with a contact time of 45 minutes. Desorption experiments were done by suspending the adsorbent that bound zinc(II) into 25 mL of HNO 3 solutions with concentration various of 0.1; 0.5; 1.0; 1.5 and 2.0 M and followed by variation of the contact time of 30; 45; 60; 75 and 90 minutes. The concentration of zinc(II) desorpted into desorption solution was determined using atomic absorption spectrophotometer. The results showed that the optimum conditions for the desorption of zinc(II) occurs in the use of 1.0 M HNO3 solution and a contact time of 60 minutes gave the percentage desorption of 93.62%. Key words: Azolla microphylla, batch, esterification, zinc(II) PENDAHULUAN Seng merupakan logam berat yang tersebar luas di lingkungan dan bahkan terdapat di perairan yang alami. Logam berat seng(II) dapat menimbulkan bahaya bagi lingkungan karena dapat terakumulasi pada makhluk hidup dan tidak dapat terdegradasi [1]. Metode 623 KIMIA.STUDENTJOURNAL, Vol.1, No. 1, pp. 623 - 628, UNIVERSITAS BRAWIJAYA MALANG Received 9 February 2015, Accepted 9 February 2015, Published online 11 February 2015