Jurnal Sains Materi Indonesia Indonesian Journal of Materials Science Vol. 13, No. 2, Februari 2012, hal : 114 - 119 ISSN : 1411-1098 114 Akreditasi LIPI Nomor : 452/D/2010 Tanggal 6 Mei 2010 MONITORING KESTABILAN DISPERSI MULTI WALL CARBON NANOTUBE DALAM SURFAKTAN HEXADECYLTRIMETHYL AMMONIUM BROMIDE Holia Onggo 1 , Djulia Onggo 2 dan R. Yudianti 1 1 Pusat Penelitian Fisika (P2F)-LIPI Jl. Cisitu 21/154D, Kompleks LIPI Bandung 40135 2 Kelompok Keahlian Kimia Fisik dan Anorganik Fakultas Matematika dan Ilmu Pengetahuan Alam (FMIPA) ITB Jl. Ganesha 10 Bandung 40135 e-mail: holi001@lipi.go.id ABSTRAK MONITORING KESTABILAN DISPERSI MULTI WALL CARBON NANOTUBE DALAM SURFAKTAN HEXADECYLTRIMETHYL AMMONIUM BROMIDE. Kestabilan dispersi Multi Wall Carbon Cano Tube (MWCNT) dalam larutan yang mengandung Hexadecyltrimethyl Ammonium Bromide (CTAB) diamati dengan UV spektrofotometer. Dispersi MWCNT dalam larutan CTAB dengan rasio massa 1: 2 dibuat dengan bantuan ultrasonic vibracell pada amplitude 60 % dengan variasi waktu sonikasi 60 menit, 90 menit dan 120 menit. Pengaruh waktu sonikasi dan waktu penyimpanan terhadap kestabilan dispersi diamati dengan mengukur absorbansi dispersi dengan UV spektrofotometer. Perubahan morfologi MWCNT akibat gelombang ultrasonik yang ditimbulkan oleh ultrasonic vibracell diamati dengan Scanning/Transmission Electron Microscope (S/TEM). Meningkatnya waktu sonikasi menyebabkan laju dispersi MWCNT meningkat ditunjukan dengan berkurangnya diameter dan panjang MWCNT. Penambahan surfaktan CTAB yang berlebihan dalam larutan menyebabkan proses sonikasi menjadi tidak efektif. Kestabilan dispersi MWCNT dapat bertahan selama 20 hari. Kata kunci: Dispersi, Sonikasi, Multi Wall Carbon Nano Tube, Hexadecyltrimethyl ammonium bromide, UV spektrofotometer. ABSTRACT MONITORING OF MULTI WALL CARBON NANOTUBE DISPERSION STABILITY OF IN HEXADECYLTRIMETHYLENE AMMONIUM BROMIDE SURFACTAN. Stability of Multi Wall Carbon Nanotube (MWCNTs) dispersion in Hexadecyltrimethylene Ammonium Bromide (CTAB) aqueous solution has been monitored using UV spectrophotometer. The dispersion was prepared from mass ratio of 1: 2, MWCNTs and CTAB using ultrasonic vibracell. The sonication has been performed for 60, 90 and 120 minutes with fixed amplitudo of 60 %. The effect of sonication time and sedimentation time to the stability of dispersion was observed by measurement of suspension absorbance by UV spectrophotometer. The morphologyical surface of MWCNT were observed by Scanning/Transmission Electron Microscope (S/TEM). Dispersion rate of MWCNTs increases by increasing sonication time. Stability of MWCNTs dispersion has been proved by formation of individual MWCNT fibers and the MWCNT dispersion could stand stable up to 20 days. Keywords: Dispersion, Sonication, Multi Wall Carbon Nano Tube, Hexadecyltrimethyl-ammonium bromide, UV spectrophotometer PENDAHULUAN Multi Wall Carbon Nano Tube (CNT) menarik banyak perhatian karena sifat listrik, mekanik dan termal yang tinggi [1,2]. Banyak penelitian yang menggabungkan CNT dengan berbagai jenis bahan lain untuk menghasilkan komposit dengan sifat mekanik dan konduktivitas listrik yang tinggi [3-6]. Pembuatan komposit dengan CNT sulit dilakukan karena daya aglomerasi dan rasio panjang terhadap diameter yang tinggi. Rendahnya dispersi CNT dalam air atau pelarut organik membatasi aplikasinya. Oleh karena itu teknik untuk mendapatkan dispersi yang homogen dan stabil merupakan kunci dalam aplikasinya untuk