AKÜ FEMÜBİD 20 (2020) 051202 (802-809) AKU J. Sci. Eng. 20 (2020) 051202 (802-809) DOI: 10.35414/akufemubid.761853 Araştırma Makalesi / Research Article Poli (Vinil klorür)/Fe 3 O 4 Manyetik Nanopartikül Kompozitlerinin Sentezi, Termal ve Elektriksel Özelliklerinin İncelenmesi Mustafa Ersin PEKDEMİR 1 1 Fırat Üniversitesi, Fen Fakültesi, Kimya Bölümü, Elazığ, Türkiye. e-posta: epekdemir@firat.edu.tr ORCID ID: https://orcid.org/0000-0002-4979-1777 Geliş Tarihi: 01.07.2020 Kabul Tarihi: 19.10.2020 Anahtar kelimeler Manyetik nanopartikül; PVC; Kompozit; Termal; Dielektrik Öz Çalışmada manyetik Fe3O4 nanopartikülleri birlikte çöktürme yöntemiyle sentezlendi. Sentezlenen nanopartiküllerin TEM ve partikül boyutlandırıcı ile boyutlarının 20 nm civarında olduğu ve XRD ile de yapılarının küre şeklinde olduğu belirlendi. VSM ile elde edilen manyetizasyon eğrisinden doygunluk manyetizasyon değeri (Ms) 53.28 emu/g olarak bulundu. Ardından Poli(vinil klorür) ile farklı yüzdelerde manyetik nanopartikül kullanılarak kompozitler hazırlandı. Hazırlanan kompozitlerin karekterizasyonu FT-IR spektrofotometresi ile yapıldı. TGA ve DSC ile termal analizleri yapıldı ve nanopartiküllerle hazırlanan kompozitlerde Tg değerlerinin saf PVC’ den daha yüksek olduğu görüldü. Elektriksel ölçüm sonuçlarından, MNP ilavesinin dielektrik sabitini düşürdüğü görüldü. Ayrıca AC iletkenliğinin artan frekansla artış göstermesine rağmen kompozitlerin iletkenliğinin saf PVC’ den daha düşük olduğu belirlenmiştir. Synthesis, Investigation of Thermal and Electrical Properties Poly(Vinyl chloride)/Fe 3 O 4 Magnetic Nanoparticle Composites Keywords Magnetic nanoparticle; PVC; Composite; Thermal; Dielectric Abstract In this study, magnetic Fe3O4 nanoparticles were synthesized by co-precipitation. It was determined that the dimensions of the synthesized nanoparticles with TEM and Particle Sizer were around 20 nm and their structures were spherical by XRD. Saturation magnetization value (Ms) from the magnetizaton curve obtained by VSM was found as 53.28 emu/g. Then, composites were prepared using Poly (vinyl chloride) with different percentages of magnetic nanoparticles. The PVC/magnetic Fe3O4 nanoparticles were characterized by FT-IR spectrophotometer. Thermal analyzes were carried out by DSC and TGA, and Tg values of composites were found to be higher than pure PVC. From the electrical measurement results, it was observed that the addition of MNP reduced the dielectric constant. Additionally, although AC conductivity increases with increasing frequency, it is determined that the conductivity of composites is lower than pure PVC. © Afyon Kocatepe Üniversitesi 1. Giriş Nanomalzemelerin sentezindeki ilerleme, nanokompozitlerin üretiminde olası kullanımlarına yönelik araştırma ilgisini canlandırmıştır (Byrne and Gun'ko 2010; Thostenson et al. 2001). Nanokompozitler, çoğunlukla polimerlerin konak görevi gördüğü konak matrislerde nanometre boyutlarında dolgu maddesi olarak hazırlanır. Nanokompozitler her zaman araştırmacıların ilgi odağı olmuştur. Bunun nedeni konak materyallerin fiziksel özellikleri, uygun şartlarda eklenen nanoboyuttaki malzemelere uygun hale gelebilmesidir. Manyetik olmayan bir materyale az miktarda manyetik nanotaneciklerin ilave edilmesi ile manyetik hale getirilebilmesi bu duruma örnek olarak gösterilebilir (Wilson et al. 2004). Benzer Afyon Kocatepe Üniversitesi Fen ve Mühendislik Bilimleri Dergisi Afyon Kocatepe University Journal of Science and Engineering