INHIBITION OF ACIDIC CORROSION OF IRON AND ALUMINIUM BY SDBS AT DIFFERENT TEMPERATURES *Sibel ZOR 1 *, Pinar Dogan', Birgiil Yazici 2  'Department of Chemistry, Faculty of Arts and Sciences,  University of Kocaeli, 41300 Kocaeli, Turkey  Department of Chemistry, Faculty of Arts and Sciences,  University of Qukurova, Adana, Turkey  ABSTRACT: The corrosion of iron and aluminium has been investigated in 0.1 Μ HCl  acidic solutions in the presence of different concentrations of SDBS at  different temperatures (303, 318, and 333 K). With this aim, the corrosion  rate of iron and aluminum was determined by using gravimetric and  potentiostatic methods. Semi-logarithmic current potential curves were drawn  by potentiostatic measurements at different temperatures. By using these  curves, the electrochemical parameters (lcorr, Ecorr, Rp) were calculated.  The activation energy (Ea) was calculated with the Arrhenius equation at  different concentrations of inhibitor. The adsorption of SDBS on metal  surface has been carried out with Langmuir adsorption isotherm and the  curves of isotherm have been obtained. According to experimental results,  SDBS is more effective in inhibiting aluminium corrosion. The inhibition  effect of SDBS decreases with an increase of temperature.  Key words: organic inhibitors, iron and aluminium corrosion, acidic  solutions  * Corresponding author: S. Zor  Email: merve@kou.edu.tr or szor2001 @yahoo.com  217 Brought to you by | Purdue University Libraries Authenticated Download Date | 5/25/15 10:26 PM