The Journal of Engineering and Exact Sciences - JCEC ISSN: 2446-9416 Vol. 03 N. 04 (2017) 0696-0704 doi: https://doi.org/10.18540/24469416030420170696 OPEN ACCESS ESTUDO DA ELETRODEPOSIÇÃO DO HIDRÓXIDO DE COBALTO APLICADO A SUPERCAPACITORES STUDY OF COBALT HYDROXIDE ELECTRODEPOSITION APPLIED TO SUPERCAPACITORS P. C. M. AGUIAR 1 , L.A. DOMÍNGUEZ 2 , J.C.M. da COSTA², R.R. PASSOS², L.A. POCRIFKA 2 1 Universidade Federal do Amazonas, Faculdade de Tecnologia, Departamento de Engenharia Química 2 Universidade Federal do Amazonas, Departamento de Química, Laboratório de Eletroquímica e Energia E-mail: priscilacm.aguiar@gmail.com RESUMO: Os supercapacitores são usados como dispositivos de armazenamento de energia e possuem alta ciclabilidade e densidade de potência. Neste estudo produziu-se e avaliaram-se filmes de hidróxido de cobalto II (Co(OH)2), promissor nesse âmbito, obtidos por meio da eletrodeposição em substrato de titânio em célula eletroquímica de quatro eletrodos (dois contra-eletrodos de platina, titânio como eletrodo de trabalho e Ag/AgCl como eletrodo de referência). Um filme fino de hidróxido de cobalto foi obtido potenciostaticamente a -1,0 V por 10 minutos utilizando CoCl2 0,1 M como eletrólito. O desempenho eletroquímico do foi investigado por meio de voltametria cíclica e teste de carga e descarga, usando-se KOH 1 M como solução eletrolítica. Foi obtida uma satisfatória capacitância máxima de 428 F.g -1 em teste de carga e descarga a 0,5 mA.cm -2 , além de ter sido possível observar comportamento pseudocapacitivo, confirmado pela espectroscopia de impedância eletroquímica. ABSTRACT: Supercapacitor is used as energy storage devices because of its high cyclability and power density. By this study were produced and evalueted cobalt hydroxide (Co(OH)2) films, promising in this context, wich were obtained by electrodeposition on titanium substrate using an electrochemical cell of four electrodes (two platinum plates as conter electrodes, titanium as working electrode and Ag/AgCl as reference electrode). A thin film of Co(OH)2 was obtained by potenciostatic deposition using CoCl2 0.1 M as electrolyte and applying - 1.0 V for 10 minutes. Electrochemical performance was investigated by cyclic voltammetry and charge and discharge test, using KOH 1 M solution as electrolyte. Is was calculated a satisfactory maximum capacitance of 428 F.g -1 when the film was subjected to 0.5 mA.cm -2 charge and discharge. Therefore, it was observed pseudocapacitive behavior, wich was confirmed by electrochemical impedance spectroscopy. 1. INTRODUÇÃO A procura por novas formas de produção de energia no futuro com o objetivo de diminuir a dependência de combustíveis convencionais e a contaminação local e global no planeta vem aumentando o interesse por materiais e processos mais adequados ao meio article info Article history: Received 20 May 2016 Accepted 3 January 2017 Available online 27 July 2017 PALAVRAS-CHAVE: Supercapacitores; Hidróxido de Cobalto; Eletrodeposição. KEYWORDS: Supercapacitor; Cobalt Hydroxide; Electrodeposition.