38 Indones. J. Math. Nat. Sci. 45(1) 2022 Indonesian Journal of Mathematics and Natural Sciences http://journal.unnes.ac.id/nju/index.php/JM Komparasi Aktivitas Fotokatalitik Ni/TiO2 dan Zn/TiO2 untuk Dekomposisi Air Menjadi H2 Sigit Priatmoko* dan Satrio B.U Prambasto Jurusan Kimia, FMIPA, Universitas Negeri Semarang, Indonesia Gedung D7 Lt.1, Kampus Sekaran Gunungpati, Semarang 50229 *E-mail: sigitwarsono65@mail.unnes.ac.id Diterima 9 Januari 2022 Disetujui 23 Maret 2022 Dipublikasikan 28 April 2022 Abstrak Telah dilakukan penelitian produksi gas hidrogen dari dekomposisi air menggunakan fotokatalitik Ni/Zn-TiO2 sebagai sumber energi alternatif yang ramah lingkungan. Tujuan penelitian adalah mempelajari pengaruh dopan logam Zn dan Ni pada padatan TiO2 terhadap aktivitas dekomposisi air untuk menghasilkan gas hidrogen. Penelitian dilakukan dengan cara impregnasi TiO2 Degussa P25 ke dalam larutan seng asetat dan nikel asetat, kemudian dikalsinasi pada temperatur yang bervariasi. Fotokatalis yang dihasilkan dikarakterisasi lebih lanjut meliputi: celah pita, kristalinitas dan SEM. Uji aktivitas fotokatalitik dilakukan di dalam reaktor, dengan menyinari air bebas mineral yang telah diberi fotokatalis menggunakan sinar tampak dan sinar UV. Produk hidrogen dianalisis dengan Gas Chromatography (GC) menggunakan detektor TCD. Hasil penelitian menunjukkan bahwa dopan Zn dan Ni pada TiO2 dapat meningkatkan produksi gas H2. Dopan logam Ni memiliki pengaruh yang lebih besar dibandingkan dengan logam Zn. Diduga hal ini disebabkan efek yang dihasilkan oleh celah pita dopan Ni lebih rendah dibandingkan dengan dopan Zn. Kata kunci: dopan, fotokatalis, celah pita Abstract The research of hydrogen gas production from water decomposition using photocatalytic Ni/Zn-TiO 2 as environmentally friendly alternative energy source has been conducted. The research objective was to study the effects of Zn and Ni metal dopants in TiO 2 solids on the activity of decomposition of water to produce hydrogen gas. The study was conducted by impregnating TiO 2 Degussa P25 to a solution of zinc acetate and nickel acetate, and then calcined at varied temperatures. The resulting photocatalysts were characterized further includes: band gap, crystallinity and SEM. Photocatalytic activity test carried out in the reactor, by irradiating a mineral-free water that has been given photocatalysts using visible and UV light. Hydrogen product was analyzed by Gas Chromatography (GC) using TCD detector. The results showed that show that both Zn and Ni dopants into TiO2 can increase the production of H2 gas. Ni metal dopants have a greater influence than the Zn metal. Presumably this is due to the effect produced by the band gap of Ni dopant is lower than the Zn dopants. Key words: dopants, photocatalyst, the band gap How to cite: Priatmoko S., & Prambasto S.B.U. (2022). Komparasi aktivitas fotokatalitik Ni/TiO2 dan Zn/TiO2 untuk dekomposisi air menjadi H2. Indonesian Journal of Mathematics and Natural Sciences, 45(1), 38-44. PENDAHULUAN Salah satu persoalan krusial yang melanda hampir seluruh wilayah di dunia termasuk Indonesia akibat bertambahnya jumlah penduduk dan meningkatnya aktivitas manusia adalah kebutuhan energi. Untuk mengatasi hal tersebut diperlukan terobosan untuk mencari sumber-sumber energi alternatif di luar energi fosil. Salah satu sumber energi yang layak dipertimbangkan adalah bahan bakar hidrogen (Liao et al., 2012; Jiang et al., 2015). Gas ini memiliki kalor pembakaran 285,5